Preparation and magnetocaloric performance of La(Fe,Co,Si) 13 alloys with wide transition temperature range
Liang Xian,Jian Yu,Weixiao Lin,Shaoqiu Ke,Chengshan Liu,Xiaolei Nie,Wanting Zhu,Ping Wei,Danqi He,Wenyu Zhao,Qingjie Zhang
DOI: https://doi.org/10.1016/j.intermet.2023.107827
IF: 4.075
2023-01-09
Intermetallics
Abstract:NaZn 13 -type La(Fe,Si) 13 alloys are one of the most promising magnetocaloric materials for room-temperature magnetic refrigeration. However, the narrow ferromagnetic-to-paramagnetic transition temperature range of La(Fe,Si) 13 alloys severely limited their magnetic refrigeration application. Herein, a series of La 1.4 Fe 11.8- x Co x Si 1.2 ( x = 0.88, 0.94, 0.98, 1.02, 1.06) alloys were designed and prepared by high-energy ball milling and annealing. It is discovered that all the samples are composed of La(Fe,Co,Si) 13 main phase and a small amount of α -Fe phase. The Curie temperature of the ferromagnetic-to-paramagnetic transition was well adjusted to room temperature by optimizing the x . A maximum magnetic entropy change (- ΔS M ) of 4.0 J kg −1 K −1 for the sample with x = 0.98 was obtained at a magnetic field of 2 T. Meanwhile, all the samples exhibit a significant increase in the half-height width of - ΔS M reaching approximately 35 K, increased by more than 41% compared with that of the reference sample prepared by arc melting. The broadened temperature range originates from the lattice distortion induced by the ball milling process. Our work indicates that La(Fe,Si) 13 alloys with relatively large - ΔS M and wide transition temperature range can be simultaneously obtained around room temperature by optimizing the composition and the ball milling process.
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering