Effect of Pre-stretch Strain at High Temperatures on the Formability of AZ31 Magnesium Alloy Sheets
Yongqiao Li,Lifei Wang,Xiaohuan Pan,Qiang Zhang,Guangsheng Huang,Bin Xing,Weili Cheng,Hongxia Wang,Kwang Seon Shin
DOI: https://doi.org/10.1007/s40195-022-01443-1
2022-01-01
Acta Metallurgica Sinica (English Letters)
Abstract:High-temperature pre-stretching experiments were carried out on the AZ31 Mg alloy at 723 K with strain levels of 2.54%,6.48%,10.92%,and 19.2%to alter the microstructure and texture for improving room-temperature formability.The results showed that the strain-hardening coefficient increased,while the Lankford value decreased.In addition,the Erichsen values of all pre-stretch sheets were enhanced compared with that of the as-received sheet.The maximum Erichsen value increased from 2.38 mm for the as-received sample to 4.03 mm for the 10.92%-stretched sample,corresponding to an improvement of 69.32%.This improvement was mainly attributed to the gradual increase in grain size,and the(0001)basal texture was weakened due to the activated non-basal slip as the high-temperature pre-stretching strain levels increased.The visco-plastic self-consistent analysis was performed on the as-received and high-temperature pre-stretched samples.Results confirmed the higher activity of the prismatic slip in 10.92%-stretched sample,leading to divergence and weakening of basal texture components.This results in an augmentation of the Schmid factor under different slip systems.Therefore,it can be concluded that high-temperature pre-stretching technology provided an effective method to enhance the formability of Mg alloy sheets.