Zirconium Nitride Derived from Layer-Structured Β-Zrncl by Deintercalation of Chlorine Layers

LP Zhu,M Ohashi,S Yamanaka
DOI: https://doi.org/10.1021/cm020580u
IF: 10.508
2002-01-01
Chemistry of Materials
Abstract:A highly oriented thin-layered zirconium nitride, ZrN, was derived from layer-structured crystals beta-ZrNCl via deintercalation of the chlorine atoms by the reaction with Na metal vapor. beta-ZrNCl consists of rhombohedrally stacked [Cl-Zr-N-N-Zr-Cl] slabs, each of which is composed of a honeycomblike double ZrN layer sandwiched between two close-packed chlorine layers. On deintercalation of the chlorine layers, the honeycomblike ZrN layers converted into ZrN(001) layers of the rock salt structure by expanding to the three equivalent directions [100] of beta-ZrNCl. beta-ZrNCl crystals were also thermally decomposed into ZrN at 950 degreesC under a stream of N-2/H-2 mixed gas. The two types of ZrNs that were obtained had the same stoichiometric composition of 1:1 but showed superconductivity at different transition temperatures (Tcs) of 6.2 and 10.0 K for the thin-layered and the thermally decomposed structures, respectively.
What problem does this paper attempt to address?