Environmentally friendly and facile Mg(OH) 2 film for electroless nickel plating on magnesium alloy for enhanced galvanic corrosion inhibition
Zhi-Hui Xie,Dan Xu,Ya Shu,Qiwen Yong,Liang Wu,Gang Yu
DOI: https://doi.org/10.1016/j.surfcoat.2024.130371
IF: 4.865
2024-01-20
Surface and Coatings Technology
Abstract:Electroless amorphous nickel (Ni)–phosphorus (P) (Ni P) alloy coatings were successfully achieved on magnesium alloys using an environmentally friendly and facile Mg(OH) 2 conversion film, followed by AgNO 3 activation. The success of the coating was confirmed through scanning electron microscopy, energy dispersive spectroscopy, and X-ray diffraction characterizations. Electrochemical tests showed that the charge transfer resistance of the newly developed electroless NiP plating coating, which had a horizontally stacked Mg(OH) 2 nanosheet primer (Mg(OH) 2 /pH 14/ENP), was significantly higher than that with a vertically grown Mg(OH) 2 nanosheet underlayer (Mg(OH) 2 /pH 10/ENP) or that with a phosphate pretreatment (ENP). The measured corrosion current density of the Mg(OH) 2 /pH 14/ENP coating was 1.08 μA cm −2 , one magnitude smaller than that of the ENP coating. Notably, the ENP coating exhibited severe galvanic corrosion, peeling off after only 24 h of the neutral salt spray (NSS) test. In contrast, the Mg(OH) 2 /pH 14/ENP surface showed no visible corrosion cavities or signs of galvanic corrosion even after 120 h of the NSS test or 21 d of exposure to a NaCl solution. These results indicate that the as-prepared coating possesses a strong inhibition capability against galvanic corrosion between the Ni layer and the magnesium alloy, providing long-lasting corrosion protection.
physics, applied,materials science, coatings & films