Ni-P deposits and non-chromate pretreatment technology on magnesium alloy

Li-yuan Niu,Guang-yu Li,Zhong-hao Jiang,Li-ping Sun,Dong Han,Jian-she Lian

DOI: https://doi.org/10.3969/j.issn.1671-5497.2006.02.002

2006-01-01

Abstract:AZ91D Magnesium alloy samples were pretreated in zinc phosphating bath, and then were plated Ni-P deposits from the bath containing nickel sulphate. The microstructure of the phosphate coatings were observed using scanning electron mioroscopy (SEM) and the phase composition were analyzed by X-ray diffractometer (XRD). The formation mechanisms of the phosphate coating and the Ni-P deposit were investigated. Result shows that chief compositions of the phosphate coating were Zn 3(PO 4) 2·4H 2O and Zn. Metal zinc crystals become the catalytic particles of the nickel deposition. The sodium metanitrobenzene suiphonate in the phosphating bath increases the micro cathode areas of the phosphate coating and accelerates the formation of the phosphate coating. It was proved that electroless Ni-P deposits onto the phosphate coating obtained from the zinc phosphating bath containing 4.0 g/L sodium metanitrobenzene suiphonate are denser and has better anticorrosion performance. The adhesion of the electroless Ni-P deposits satisfies the requirement of ISO 2819.