High Corrosion Resistance of Electroless Ni-P with Chromium-Free Conversion Pre-Treatments on AZ91D Magnesium Alloy

J. Sudagar,Lian Jian-she,Chen Xiao-min,Lang Peng,Liang Ya-qin

DOI: https://doi.org/10.1016/s1003-6326(11)60802-9

IF: 3.752

2011-01-01

Transactions of Nonferrous Metals Society of China

Abstract:Phosphate-manganese, tannic acid and vanadium conversion coatings were proposed as an effective pre-treatment layer between electroless Ni-P coating and AZ91D magnesium alloy substrate to replace the traditional chromate plus HF pre-treatment. The electrochemical results show that the chrome-free coatings plus electroless Ni-P coating on the magnesium alloy has the lowest corrosion current density and most positive corrosion potential compared with chromate plus electroless Ni-P coating on the magnesium alloy. These proposed pre-treatment layers on the substrate reduce the corrosion of magnesium during plating process, and reduce the potential difference between the matrix and the second phase. Thus, an electroless Ni-P coating with fine crystalline and dense structure was obtained, with preferential phosphorus content, low porosity, good corrosion-resistance and strengthened adhesion than the chromate plus electroless Ni-P.