Abstract:More and more composite materials have been being utilized in nuclear facilities. While the external loading applied, the stress in composite is concentrated, which is harmful and may cause interfacial damage. The debonding and sliding at the interface between matrix and particles are the most common phenomena. In this paper, a statistically elastoplastic constitutive model for particle-dispersed composites is developed by accounting stochastically for both interfacial damage and localized plasticity. The effects of damaged interface on the strain field in composite are considered in two ways. First, the damaged interface between the matrix and the particles makes the strain field inside inclusions is different from that of the particles with perfectly bonded interface. Second, it contributes an additional strain, which is due to the displacement jump at the matrix-inclusion interface. This additional is defined as an integration of displacement jumps between the matrix and the particles over their interface. In present paper, the first part is considered by using a modified Eshelby’s S-tensor. After deriving the local relative displacement distributions between matrix and inclusion at the interface, the second contribution of damaged interface to the average strain can be expressed in terms of the corresponding eigen-strain or the uniform external loading, by introducing the damage-relevant tensors, which are transformation tensors and tends to zero if interfacial damage does not take place. Both the tangential and normal discontinuities at the interface are independently modeled. The model uses statistic scheme with distribution functions in the stress/strain space, so that the meso-local effects of plastic deformation, interfacial damage and their interactions are accounted for. In order to verify the feasibility and performance of the proposed constitutive model, numerical calculations are carried out. It is found that the damaged interface conditions of debonding and/or sliding give detrimental effects on the overall properties of composites. Thus, the establishment of the most appropriate model describing properly the meso-local phenomena.

DYNAMIC STRESS ANALYSIS OF THE INTERFACE IN A PARTICLE-REINFORCED COMPOSITE

Micro Failure Analysis of Fiber Metal Laminates

An elastic-plastic cohesive zone model for metal-ceramic interfaces at finite deformations

Theoretical Analysis on the Local Critical Stress and Size Effect for Interfacial Debonding in Particle Reinforced Rheological Materials

Analysis of Particle-Dispersed Composites Accounting Stochastically for Interfacial Damage

An Anti-Interpenetration Model and Connections Between Interphase and Interface Models in Particle-Reinforced Composites

Internal Stress Distribution and Cracking Around Flaws and Openings of Rock Block under Uniaxial Compression: A Particle Mechanics Approach

Interaction of Multiple Micro-Defects on the Strength and Failure Mechanism of UD Composites by Computational Micromechanics

Dynamic Failure Analysis Of Bimaterial Beam With Crack-Tip Terminating Interface

DYNAMIC FRACTURE MECHANICS ANALYSIS FOR ANTIPLANE CRACKS IN NONHOMOGENEOUS COMPOSITE MATERIAL

Modeling of progressive debonding of interphase- matrix interface cracks in particle reinforced composites using VCFEM

A Micromechanical Debonding Analysis of Fiber-Reinforced Composites Due to Curing Residual Stress

Dynamic Fracture Mechanics Analysis for Composite Material with Material Non-Homogeneity in Thickness Direction

541 Modeling of particle dispersed composite with meso-scale delamination or sliding

Simulation of the fracture behavior of inclusion-matrix interface for particle reinforced composites

Micromechanical Analysis of SiC/Ti6Al4V Composite Under Complex Stress State

Homogenized Finite Element Analysis on Effective Elastoplastic Mechanical Behaviors of Composite with Imperfect Interfaces

DYNAMIC FRACTURE ANALYSIS OF CRACK AT BIMATERIAL INTERFACE

Creep and Stress Relaxation Behavior of Metal Matrix Particulate Composites Induced by Interface Diffusion with Coupled Thermomechanical Strains

Interfacial effect on mechanical behaviors of bidirectional-fiber-reinforced composites

Stress Transfer Model and Micromechanic Analyses of Unidirectional Single-short-fiber Composite