Abstract:Solar cells based on kesterite-type $Cu_2ZnSnS_4$ (CZTS) thin films were fabricated using a chemical route to prepare the $CZTS$ films, consisting in sequential deposition of $Cu_2SnS_3$ (CTS) and $ZnS$ thin films followed by annealing at $550^\circ C$ in nitrogen atmosphere. The $CTS$ compound was prepared in a one-step process using a novel chemical procedure consisting of simultaneous precipitation of $Cu_2S$ and $SnS_2$ performed by diffusion membranes assisted $CBD$ (chemical bath deposition) technique. Diffusion membranes were used to optimize the kinetic growth through a moderate control of release of metal ions into the work solution. As the conditions for the formation in one step of the $Cu_2SnS_3$ compound have not yet been reported in literature, special emphasis was put on finding the parameters that allow growing the $Cu_2SnS_3$ thin films by simultaneous precipitation of $Cu_2S$ and $SnS_2$. For that, we propose a methodology that includes numerical solution of the equilibrium equations that were established through a study of the chemical equilibrium of the system $SnCl_2$, $Na_3C_6H_5O_7\cdot 2H2O$, $CuCl_2$ and $Na_2S_2O_3\cdot5H_2O$. The formation of thin films of $CTS$ and $CZTS$ free of secondary phases grown with a stoichiometry close to that corresponding to the $Cu_2SnS_3$ and $Cu_2ZnSnS_4$ phases, was verified through measurements of X-ray diffraction $(XRD)$ and Raman spectroscopy. Solar cell with an efficiency of $4.2%$, short circuit current of $16.2 mA/cm^2$ and open-circuit voltage of 0.49 V was obtained.

Fabrication of Cu2znsns4 Screen Printed Layers for Solar Cells

Preparation of Cu2znsns4 Film by Printing Process for Low-Cost Solar Cell

Low-cost Fabrication of Cu 2 ZnSnS 4 Thin Films for Solar Cell Absorber Layers

Chemical synthesis of Cu(In) metal inks to prepare CuInS2 thin films and solar cells

Fabrication of Cu 2 ZnSnS 4 thin films using oxides nanoparticles ink for solar cell

Cu–In Intermetallic Compound Inks for CuInS 2 Solar Cells

Cuins2 Thin Film Prepared by Molecular-Solution Printing Technology and Its Photovoltaic Properties

Fabrication and Microstructure of P-Type Transparent Conducting Cus Thin Film and Its Application in Dye-Sensitized Solar Cell

Synthesis and Characterization of Hydrazine Solution Processed Cu12Sb4S13 Film

Cu2znsns4 Solar Cell Prepared Entirely by Non-Vacuum Processes

Fabrication of solar cells based on $Cu_2ZnSnS_4$ prepared from $Cu_2SnS_3$ synthesized using a novel chemical procedure

Fabrication of Cu2ZnSn(SxSe1 − X)4 Solar Cells by Ethanol-Ammonium Solution Process

Perovskite solar cells based on screen-printed thin films

Nanoparticle-based screen printing of copper zinc tin sulfide thin film as photocathode for quantum dot sensitized solar cell

Stable, carbon-free inks of Cu2ZnSnS4 nanoparticles synthesized at room temperature designed for roll-to-roll fabrication of solar cell absorber layers

Fabrication of Metal Grid on Silicon-Based Solar Cell by Electrochemical Deposition and Microcontact Print

Hydrazine Processed Cu2SnS3 Thin Film and Their Application for Photovoltaic Devices

Study on the Non-Vacuum Printing Technology for the Fabrication of CuInSe_2 Thin Film Solar Cell

Fabrication of Cu 2 SnS 3 thin-film solar cells with oxide precursor by pulsed laser deposition

Low Cost Preparation of Cu2ZnSnS4 and Cu2ZnSn(SxSe1−x)4 from Binary Sulfide Nanoparticles for Solar Cell Application

Flexible CuS nanotubes-ITO film Schottky junction solar cells with enhanced light harvesting by using an Ag mirror