Abstract:Quaternary chalcogenide Cu 2 CoSnS 4 (CCTS) thin films were successfully prepared by spray pyrolysis on glass substrates in varying the precursor concentration and the thiourea volume. The effects of the precursor concentration and the thiourea volume on the formation of the CCTS phase were systematically investigated by X-ray diffraction, Raman spectroscopy, Energy-Dispersive X-ray Spectroscopy. The electrical resistivity at room temperature has been measured by the four probes method. It is shown that the crystallization of the stannite CCTS phase depends on both the precursor concentration and thiourea volume. The minimum volume of thiourea required to crystallize the CCTS phase depends on the precursor concentration, i.e. the CCTS crystallization needs higher volume of thiourea at low precursor concentration. For higher precursor concentration, the CCTS is poorly crystallized with the presence of secondary phases such as CuS 2 , CoS 2 , and CuCo 2 S 4 , while the crystallization domain is relatively large. The CCTS well crystallizes only in a narrow range of precursor concentration and thiourea volume. The relatively poor crystallization combined with the presence of secondary phases are harmful for the optical and electrical features of the CCTS film. Besides, optical transmission measurements of the optimized film showed an optical gap of 1.7 eV (~ 730 nm) and an absorption coefficient included between 10 4 and 10 5 cm −1 in the visible solar range. Furthermore, the optimized stannite CCTS films are compact exhibiting a relatively rough and granular surface due to the formation of copper sulfide nodules. The electrical resistivity of the optimized CCTS film is about 0.4 10 –2 Ω cm. These results suggest that the deposited films fit the requirements of absorbing layer in solar cells. The diode composed of Au/Cu 2 CoSnS 4 /SnO 2 films was investigated with current–voltage ( I – V ) measurements performed under dark and bright conditions. The series resistance, saturation current and ideality factor of typical diode is estimated to be 689 Ω, 1.15 10 –5 A and 3, respectively.

Fabrication of Cu 2 SnS 3 thin-film solar cells with oxide precursor by pulsed laser deposition

Fabrication of Cu2SnS3 Thin Film Solar Cells Via a Sol-Gel Technique in Air

Fabrication of highly crystallized Cu 2 SnS 3 thin films through sulfurization of Sn-rich metallic precursors

Low-cost Fabrication of Cu 2 ZnSnS 4 Thin Films for Solar Cell Absorber Layers

Fabrication of Cu2SnS3 Thin Films by Ethanol-Ammonium Solution Process by Doctor-Blade Technique

Fabrication of Cu 2 ZnSnS 4 thin films using oxides nanoparticles ink for solar cell

The photovoltaic properties of novel narrow band gap Cu2SnS3 films prepared by a spray pyrolysis method

Fabrication of solar cells based on $Cu_2ZnSnS_4$ prepared from $Cu_2SnS_3$ synthesized using a novel chemical procedure

Effect of the stacking order, annealing temperature and atmosphere on crystal phase and optical properties of Cu2SnS3

All-Layer Sputtering-Free Cu2Zn1-xCdxSnS4 Solar Cell with Efficiency Exceeding 7.5%

Facile Fabrication of Cu2ZnSnS4 Thin Film Based on a Novel Metal–salt Precursor Printing Route

Preparation and Characterization of Cuins2 Thin Films for Solar Cells by Chemical Bath Deposition

Fabrication of Cu2ZnSn(SxSe1 − X)4 Solar Cells by Ethanol-Ammonium Solution Process

Preparation And Characterization Of Cu2znsns4 Thin Films And Solar Cells Fabricated From Quaternary Cu-Zn-Sn-S Target

Preparation and Characterization of Cu2SnS3 Thin Films by Two Stage Process for Solar Cell Application

Fabrication of Cu2Sn1-xGexS3 Thin-Film Solar Cells via Sulfurization of Cu2GeS3/Cu2SnS3 Stacked Precursors

Fabrication of Cu 2 ZnSnS 4 absorber layers with adjustable Zn/Sn and Cu/Zn+Sn ratios

A 5.5% efficient co-electrodeposited ZnO/CdS/Cu 2 ZnSnS 4 /Mo thin film solar cell

Hydrazine Processed Cu2SnS3 Thin Film and Their Application for Photovoltaic Devices

Synthesis of Cu2CoSnS4 chalcogenide thin films by spray pyrolysis and efficient Au/p-CCTS/n-SnO2 diode for cells solar applications

Preparation of Cu2znsns4-Based Thin Film Solar Cells by A Combustion Method