Abstract:In this investigation, the influence of aging time on Cu2ZnSnS4 precursor solutions is assessed, revealing an association reaction among Cu2+, thiourea, and carboxyl groups. The incorporation of hydrochloric acid inhibits this reaction, diminishes the concentration of VSn(−/0) and CuSn(−/0) defects, and mitigates the band‐tailing effect, thereby attaining an optimal efficiency of 11% in a Cu2++Sn2+ system without MgF2. The Sol‐gel precursor solution reaction mechanism has a significant impact on the Cu2ZnSn(S, Se)4 (CZTSSe) solar cells. It is discovered that in the Cu2ZnSnS4 (CZTS) precursor solution (CZTS‐PS) in the preparation, there is an association reaction among Cu2+, thiourea (Tu), and carboxyl (‐COOH), which is an important reason for the undesirable CZTSSe solar cells. The strong association reaction generates excessive Cu2+ ions, forming the CuxSe secondary phase on the surface of the CZTSSe absorber. The secondary phase causes a short circuit and deterioration of gadget performance. Following a 6‐h aging period for the CZTS‐PS, the average photoelectric conversion efficiency (PCE) of the device is enhanced to 8.02%, and there is also an improvement in device uniformity, as evidenced by a decrease in the standard deviation to less than 1. To inhibit the association reaction and eliminate the aging time phenomenon, a strategy is developed using hydrochloric acid to regulate the CZTS‐PS environment. This strategy shifts the REDOX reaction in Cu2++Sn2+ toward the formation of Cu1++Sn4+, leading to a decrease in the defect concentrations of VSn(−/0) and CuSn(−/0), which increases the carrier concentration and reduces the impact of band tailing. The average power conversion efficiency (PCE) of the devices improved from 7.45% to 9.26%, the PCE of the best‐performing CZTSSe solar cells increased from 9.25% to 9.83%, and the consistency among the devices is further enhanced, as indicated by a reduction in the standard deviation from 0.98 to 0.44. Ultimately, the device performance of the Cu2++Sn2+‐DMF system improved by 11.01% (without the MgF2 layer) after optimization. This study serves as a reference for regulating the environment of the CZTS‐PS to further enhance the CZTSSe devices' performance, and the photoelectric conversion efficiency is improved by ≈30%.

Improving the efficiency of Cu2ZnSnS4 solar cells by promoting the homogeneous distribution of Sn element

Formation of Alloyed Cu2Cox Zn1-x Sn(S,Se)4 Absorption Layer and Its Application in Solar Cells

Formation of Alloyed Cu2CoxZn1-xSn(S,Se)4 Absorption Layer and Its Application in Solar Cells.

Improved Cu2ZnSnS4 Solar Cell Performance by Multimetallic Stacked Nanolayers

All-Layer Sputtering-Free Cu2Zn1-xCdxSnS4 Solar Cell with Efficiency Exceeding 7.5%

Heterojunction post-heat treatment process driving high efficiency for Cu2ZnSnS4 solar cell

Preparation of High-Quality Cu2ZnSnS4 Thin Films for Solar Cells Via the Improvement of Sulfur Partial Pressure Using a Static Annealing Sulfurization Approach

Low-cost Fabrication of Cu 2 ZnSnS 4 Thin Films for Solar Cell Absorber Layers

Over 10% Efficient Cu2CdSnS4 Solar Cells Fabricated from Optimized Sulfurization

All Solution-Processed Cu2znsns4 Solar Cell By Using High-Boiling-Point Solvent Treated Ball-Milling Process With Efficiency Exceeding 6%

Investigation of Zn/Sn ratio for improving the material quality of CZTS thin films with the reduction of Cu2-xS secondary phase

Surprising Efficiency Enhancement of Cu 2 ZnSn(S,Se) 4 Solar Cells with Abnormal Zn/Sn Ratios

Se as hetero-nucleation seeds reinforcing intermetallic diffusion for improved electrodeposition-processed CZTS solar cells

Improvement of grain growth and composition distribution of Cu2ZnSn(S,Se)4 by using chloride-based precursor solution

Improved Performance of Electroplated CZTS Thin-Film Solar Cells with Bifacial Configuration

Preparation And Characterization Of Cu2znsns4 Thin Films And Solar Cells Fabricated From Quaternary Cu-Zn-Sn-S Target

Influence of sulfur partial pressure on the structural performance of Cu2ZnSnS4 solar cells

Optimization of the Selenization Pressure Enabling Efficient Cu 2 ZnSn(S,Se) 4 Solar Cells

Enhance the Performance of CZTSSe Solar Cells Through Inhibiting the Cu2+, Tu, and (─COOH) Association Reaction

Efficiency improvement for post-sulfurized CIGS solar cells enabled by in situ Na doping

Passivating SnZn Defect and Optimizing Energy Level Alignment via Organic Silicon Salt Incorporation toward Efficient Solution‐Processed CZTSSe Solar Cells