Abstract:The Er3+-doped Al2O3 films were prepared by sintering Er-ion-implanted γ-AlOOH xerogel films on SiO2/Si(100) substrates. In a cycle, the γ-AlOOH xerogel films about 50 nm thick were dip-coated using aluminium isopropoxide-derived γ-AlOOH sols; the Er ions were then implanted into the γ-AlOOH xerogel films using an ion energy of 45 keV with different doses of 5×1014 to 1×1016 ions cm−2. Er3+-doped Al2O3 films were formed after 1, 2, and 4 cycles of dip-coating and implantation at different sintering temperatures of 800–1200 °C. The photoluminescence (PL) spectra were observed with a main peak at 1.533 μm and a side peak at 1.549 μm for all the Er3+-doped Al2O3 films. The intensity of PL peak of the Er3+-doped Al2O3 film obtained after 4 cycles with 5×1015 ions cm−2 dose at every cycle and sintered at 900 °C for 5 h, increased by about 10 and 3 times compared with that of the films obtained after 1 and 2 cycles. At the same sintering temperature of 900 °C, the intensity of PL peak of the Er3+-doped Al2O3 films first increased with the increase of dose from 5×1014 to 5×1015 ions cm−2 at every cycle, and then a saturation tendency was observed when the dose further was increased to 1×1016 ions cm−2. For the samples using 5×1015 ions cm−2 dose at every cycle, the PL intensity increased with the increase of sintering temperature from 800 to 1200 °C.

Fabrication and Photoluminescence Characteristics of Nonuniform Yb-Er Codoped Films

Chemical Combustion Synthesis and Up-Conversion Properties of Er3+ Doped Yb3Al5O12 Powder

Correlation Of Efficient Luminescence With Crystal Structures Of Y-Er2si2o7 And Alpha-Er2si2o7 In Er-Doped Silicon Oxide Films

Yb3+ → Er3+ Energy Transfer in Al2O3 and Temperature Characteristic of Near-Infrared Photoluminescence

Correlation of Efficient Luminescence with Crystal Structures of Y-Er2si2o7 and Α-Er2si2o7 in Er-doped Silicon Oxide Films

Effects of Yttrium Codoping on Photoluminescence of Erbium-Doped TiO2 Films

Photoluminescence Performance of Er/Yb Co-Doped NBT Ceramics Prepared Via Hydrothermal Method

Control of the Formation and Luminescent Properties of Polymorphic Erbium Silicates on Silicon

Photoluminescence and Its Physical Mechanism of Er/Yb Co-Doped Borate-Silicate Glass

Coherent effect of Er3+–Yb3+ co-doping on enhanced photoluminescence properties of Al2O3 powders by the sol–gel method

Photoluminescence Properties of Er3+-doped Al2O3 Film Synthesized from Er-ion-implanted Γ-Alooh Xerogel

Preparation and up-conversion luminescence of β-SiAlON:Ln3+ (Ln=Yb/Ho, Yb/Er) microparticles

Research on optical properties of Yb3+/Er3+ co-doped oxy-fluoride glass

Up-Conversion Mechanisms of Yb-Er Co-Doped Al2o3 Film and Its Temperature Characteristics

Fabrication and characterization of highly luminescent Er3+:Al2O3 thin films with optimized growth parameters

Preparation of Li and Er Codoped ZnO Thin Films and Their Photoluminescence

Preparation and Near-Infrared Luminescence Properties of Y 2 O 3 :Er 3+ , Yb 3+ Nanopowders

Fluorescence Enhancement and Structural Development of Sol–gel Derived Er3+-doped SiO2 by Yttrium Codoping

Fabrication and characterization of Er,Ndcodoped Y2O3 Transparent Ceramic: A dual mode Photo-luminescence emitter

Photoluminescence and electroluminescence of erbium yttrium and ytterbium co-doped Er silicates

Photoluminescence and Energy Transfer Processes in Rare Earth Ion Doped Oxide Thin Films with Substrate Heating