La[sub 0.85]sr[sub 0.15]mno[sub 3−δ] Infiltrated Y[sub 0.5]bi[sub 1.5]o[sub 3] Cathodes for Intermediate-Temperature Solid Oxide Fuel Cells

Zhiyi Jiang,Changrong Xia,Fei Zhao,Fanglin Chen

DOI: https://doi.org/10.1149/1.3099321

2009-01-01

Abstract:Porous yttria-stabilized bismuth oxides (YSB) were investigated as the backbones for La0.85Sr0.15MnO3-delta (LSM) infiltrated cathodes in intermediate-temperature solid oxide fuel cells. The cathodes were evaluated using anode-supported single cells with scandia-stabilized zirconia as the electrolytes. With humidified H-2 as the fuel, the cell showed peak power density of 0.33, 0.52, and 0.74 W cm(-2) at 650, 700, and 750 degrees C, respectively. At 650 degrees C, the cell polarization resistance was only 1.38 Omega cm(2), < 50% of the lowest value previously reported, indicating that YSB is a promising backbone for the LSM infiltrated cathode.