Abstract:The effect of composition tuning on glass forming ability (GFA), mechanical properties and atomic structure in ZrxCo84−xAl16 bulk metallic glasses (BMGs) with x = 51–58 has been investigated by using copper-mold suction casting, nanoindentation, high-energy X-ray diffraction, extended X-ray absorption fine structure experiments and ab initio molecular dynamics simulations, respectively. It is found that GFA firstly increases then decreases with increasing Zr content, exhibiting a maximum diameter of 7 mm with the Zr content of 55 and 56, while an abrupt reduction of bending plasticity occurs as the Zr content drops below 55. Both experimental and theoretical results find that GFA is remarkably enhanced, due to the abnormal reduction in the fractions of the Co-centered ⟨0, 2, 8, 1⟩, ⟨0, 3, 6, 2⟩ and ⟨0, 3, 6, 3⟩ polyhedra, and the denser atomic packing of Zr atoms around center Co atom, as the Zr content increases from 51 to 56. Meanwhile, the simultaneously improved plasticity is associated with the increased Co-centered ⟨0, 3, 6, 0⟩, and Al-centered ⟨0, 2, 8, 1⟩ and ⟨0, 3, 6, 2⟩ polyhedra, which provide more fertile sites for the nucleation of shear transformations. Further Zr addition to 58 increases remarkably the fractions of Zr- and Al-centered ⟨0, 1, 10, 2⟩ and ⟨0, 3, 6, 4⟩ polyhedra, and causes looser atomic packing of Co atoms around center Zr atom, leading to the reduction in GFA. However, the plasticity is not enhanced further but remains nearly constant, which may be related to the deteriorated effect on plasticity of the decreased fractions of Zr-centered ⟨0, 1, 10, 5⟩ and Co-centered ⟨0, 3, 6, 0⟩ polyhedra, and the increased fractions of Zr-centered ⟨0, 1, 10, 3⟩ and ⟨0, 2, 8, 4⟩ and Co-centered ⟨0, 2, 8, 0⟩ polyhedra. Compositional tuning, with internal structure tuned to favor both GFA and plastic flow, offers new possibilities in developing ductile BMG materials.

New Glassy Zr-Al-Fe and Zr-Al-Co Alloys with A Large Supercooled Liquid Region

High-strength Cu-based bulk glassy alloys in Cu–Zr–Ti and Cu–Hf–Ti ternary systems

Cu-based bulk glassy alloys with high tensile strength of over 2000 MPa

Cu-Based Bulk Glassy Alloys with Good Mechanical Properties in Cu-Zr-Hf-Ti System

Formation, Thermal Stability and Mechanical Properties of Zr-Nb-Cu-Ni-Al Bulk Metallic Glasses

Structural Properties and Thermal Stability of Glassy (Zr<sub>.65</sub>Al<sub>.075</sub>Cu<sub>.175</sub>Ni<sub>.1</sub>)<sub>100-x</sub>Fe<sub>x</sub> (x≤20) Alloys Prepared by Mechanical Alloying

Formation of a Ni- and Be-free Zr-based glassy alloy in centimeter scale

Unusual Solidification Behavior of a Zr–Cu–Ni–Al Bulk Glassy Alloy Made from Low-Purity Zr

A Novel Ni-Free Zr-Based Bulk Metallic Glass with High Glass Forming Ability, Corrosion Resistance and Thermal Stability

Glass forming ability and bending plasticity evolutions in Zr-Co-Al bulk metallic glasses and their structural origin

A Ti-based bulk glassy alloy with high strength and good glass forming ability

Enhanced Plasticity in a Zr-based Bulk Metallic Glass Containing Nanocrystalline Precipitates

Structural Properties and Thermal Stability of Glassy (Zr.65al.075cu.175ni.1)100-Xfex (x≤20) Alloys Prepared by Mechanical Alloying

Preparation, Characterization, and Properties of Novel Ti-Zr-Be-Co Bulk Metallic Glasses.

Formation and ultrahigh mechanical strength of multicomponent Co-based bulk glassy alloys

Formation of Ni–Nb–Zr–X (X = Ti, Ta, Fe, Cu, Co) Bulk Metallic Glasses

Crystallization and mechanical behavior of (Hf, Zr)–Ti–Cu–Ni–Al metallic glasses

A Ti–Zr–Be–Fe–Cu Bulk Metallic Glass with Superior Glass-Forming Ability and High Specific Strength

Crystallization behavior of ZrAlNiCu bulk metallic glass with wide supercooled liquid region

Incorporation of ultrafine nanograins in Zr–Cu–Al–Ni–Co bulk metallic glass enabling significantly improved mechanical properties

Effect of Al Composition Tuning on Properties and Structure in Zr-Co-Al Metallic Glass