Abstract:Single-crystal BaSO4 nanofibers and multi-architecture bundles were successfully synthesized in sodium bis(2-ethylhexyl) sulfosuccinate (AOT)-based microemulsions containing K2S2O8 and BaCl2, in which the controlled release of SO42- ions was realized in situ by the radiolytic reduction of S2O82- ions. The molar ratio of water to surfactant (omega values), the counterions of Ba2+, and the addition of aromatic compounds into the oil phase of the microemulsions were used to adjust the yield of hydrated electrons (e(aq)(-)). This allowed for controlling the reduction of S2O82- ions and the release of SO4 2-ions, leading to the shape manipulation of BaSO4 nanoparticle. With an increase in omega values or dose rate, the yield of e(aq)(-) increased, which led to a quicker release of SO42- ions, and this did not favor the formation of BaSO4 nanofibers. When BaCl2 was replaced with Ba(NO3)(2) the formation of nanofilaments became possible at a higher dose rate and a higher omega value, because NO3- effectively decreased the yield of e-aq and the rate of S2O82- ion reduction. When toluene was added into the oil phase of the microemulsions, the excess electrons were effectively scavenged in the oil phase, and the concentration of e-aq in the water pool decreased. This favored the formation of nanofibers at higher dose rates. These results showed that the mechanism about morphology control by the yield of e(aq)(-) was verified in the syntheses of BaSO4 nanoparticle.

Preparation of BaSO4 nanoparticles in non-ionic w/o microemulsions

Preparation of barium sulfate submicro-particles with high purity by solventing-out process

Preparation of ultrafine barium sulfate particle using a water/oil microemulsion

Preparation of barium sulfate particles using filtration dispersion precipitation method in O/W system

Synthesis of BaCO 3 with Different Morphologies Using Amphiphilic PS-PAA Copolymer As Medium

COMPOSITION AND STABILITY OF W/O MICROMULSIONS FOR PREPARATION OF BaSO4 NANOPARTICLES

Preparation of Core-Shell Polycarbonate/BaSO_4 Submicron Composite Particles

Process intensification of BaSO4 nanoparticle preparation with agitation of microbubbles

Synthesis of BaSO4 Nanofibers Controlled by the Yield of Hydrated Electrons in AOT-Based Microemulsions

Stability and Synthesis of Barium Fluoride Nanoparticles from CTAB/Butanol/Heptane/Water Microemulsion System

Room-Temperature Synthesis of BaTiO<sub>3</sub>Nanoparticles in Large Batches

Preparation of Polystyrene/Sio2 Composite Nanoparticles Bearing Sulfonic Groups on the Surface Via Emulsion Copolymerization Using A Polymerizable Emulsifier

Synthesis of Highly Dispersed Barium Titanate Nanoparticles by a Novel Solvothermal Method

Sonochemical Syntheses Of Baf2 Nanoparticles And Cubes

Growth of BaWO4 Fishbone-Like Nanostructures in W/o Microemulsion.

Preparation of Monodisperse Nanocrystalline Barium Titanate

Preparing Ultrafine Barium Sulfate Particles Using Membrane-Dispersion-precipitation Technology

Radiolytic Synthesis of BaSO4 Microspheres

Preparation of A Monodispersed Suspension of Barium Titanate Nanoparticles and Electrophoretic Deposition of Thin Films

Reuse of Microemulsion for Preparing Barium Sulfate Nanoparticles Through Breaking the Microemulsion by Distillation

Miniemulsification of butyl acrylate containing nanometer silica particles