Preferred Crystalline Orientation of Melt-Spun Nd-Fe-M-B Flakes (M=ti/zr/hf/v/nb/ta)

TS CHIN,SH HUANG,JM YAO

DOI: https://doi.org/10.1109/20.179421

IF: 1.848

1992-01-01

IEEE Transactions on Magnetics

Abstract:Preferred crystalline orientation of Melt-spun Nd13Fe80-xMxB6 flakes (M= 0.5 to 3 at% of Ti, Zr, Hf, V, Nb or Ta) prepared by single roller melt spinning were studied by x-ray diffractometry, microstructure and magnetic measurements. Certain alloying elements, M= Ti, Zr, V and Ta, enhance both preferred crystalline orientation and coercivity at moderate wheel speeds, V(s), typically 8 to 15m/s. The degree of preferred orientation calculated from x-ray diffraction patterns is higher than 50% across the whole thickness, at V(s)= 8 and 10 m/s, despite the apparent equiaxed grains. Magnetic measurements on spun flakes and field aligned pulverized powders show highly anisotropic behavior. They have potential applications for anisotropic resin bond magnets.