Abstract:Magnesium aluminate (MgAl2O4) spinel has grasped considerable attention in high-temperature application by right of its excellent properties. However, the poor sintering behavior of MgAl2O4 is detrimental to its further development. In the present work, the application of isostructural heterogeneous nucleation method provides a novel idea for optimizing the sintering behavior of refractory materials. A series of (1-x)MgAl2O4-xMg2TiO4 (x = 0, 0.02, 0.04, 0.06, 0.08, and 0.1) spinel solid solutions with a present ration of components were fabricated from light calcined magnesia, reactive alumina and pre-preparation Mg2TiO4. The effect of Mg2TiO4 heterogeneous nucleating agent on the crystalline phase, densification, and microstructure evolution of MgAl2O4–Mg2TiO4 spinel solid solutions was studied. The XRD, XPS, and EDS results showed that Mg2TiO4 entered the lattice of MgAl2O4 to form a spinel solid solution, and the heterovalent substitution process was identified, where Ti4+ and Mg2+ ions of larger radius in the Mg2TiO4 replaced the Al3+ of smaller radius in the MgAl2O4. For the sample at x = 0.08, the spinel solid solutions exhibited the optimized densification with a relative density of 93.3%, an apparent porosity of 1.2%, and a compressive strength of 84.5 MPa. A significant increase in densification was related to the lattice distortion induced by ion size mismatch during the heterovalent substitution, thus accelerating the diffusion rate of Mg2+ and Al3+ ions in the spinelisation state. Moreover, the solid solubility content of Ti4+ in the MgAl2O4–Mg2TiO4 spinel solid solutions had a significant effect on the grain morphologies. The Mg2TiO4 heterogeneous nucleating agent significantly increased the spinelisation rate of MgAl2O4 spinel with negligible effect on densification.

In-situ Synthesized Mg-AL Spinel at Low Temperature Used Chloride Ion Mg-AL Hydrotalcites

Self-Propagating High-Temperature Synthesis of Magnesium Aluminate Spinel Using Mg–Al Alloy

Effect of Synthetic Parameters on Synthesis of Magnesium Aluminum Spinels

Microwave idrothermal synthesis of magnesium-aluminium spinel

Synthesis of MgAl2O4 Spinel in a Thermal Plasma

Low-temperature synthesis of micro/nano Lithium Fluoride added magnesium aluminate spinel

Sintering behavior and microstructure of (1-x)MgAl2O4-xMg2TiO4 spinel solid solutions prepared by isostructural heterogeneous nucleation

Novel Synthesis of High Surface Area MgAl2O4 Spinel As Catalyst Support

The low temperature fabrication of nanocrystalline MgAl2O4 spinel aerogel by a non-alkoxide sol-gel route

Synthesis and Characterization of Porous Magnesium Aluminate Spinel by Hydrothermal Process

Facile sol-gel synthesis of ZnAl2O4 spinel nanoceramics for photocatalytic applications: H2 production and MB dye degradation

From layered double hydroxide to spinel nanostructures: facile synthesis and characterization of nanoplatelets and nanorods

Polyol-mediated synthesis and characterization of magnesium–aluminum spinel nanoparticles

Low-temperature synthesis of MgxCo1-xCo2O4 spinel catalysts for N2O decomposition

Preparation of Magnesium Aluminate Spinel Nanofibers with High Temperature Resistance by Electrospinning Process Based on Non-Hydrolytic Sol-Gel Method

Effect of different MgO/Al2O3 ratios on microstructural densification, sintering process and mechanical property of MgAl2O4 materials

Preparation and Characterization of Novel Nonstoichiometric Magnesium Aluminate Spinels

Physical Properties of MgAl2O4, CoAl2O4, NiAl2O4, CuAl2O4, and ZnAl2O4 Spinels Synthesized by a Solution Combustion Method

A strategy for controlling microstructure and mechanical properties of microporous spinel (MgAl2O4) aggregates from magnesite and Al(OH)3

Effect of pH on the chemical composition, morphology, and densification of magnesium aluminate spinel nanopowder synthesized by the coprecipitation method

Novel Colloidal Silica Technology For In Situ Spinelization in MgO-Containing Refractories