Abstract:Magnesium aluminate (MgAl2O4) spinel has grasped considerable attention in high-temperature application by right of its excellent properties. However, the poor sintering behavior of MgAl2O4 is detrimental to its further development. In the present work, the application of isostructural heterogeneous nucleation method provides a novel idea for optimizing the sintering behavior of refractory materials. A series of (1-x)MgAl2O4-xMg2TiO4 (x = 0, 0.02, 0.04, 0.06, 0.08, and 0.1) spinel solid solutions with a present ration of components were fabricated from light calcined magnesia, reactive alumina and pre-preparation Mg2TiO4. The effect of Mg2TiO4 heterogeneous nucleating agent on the crystalline phase, densification, and microstructure evolution of MgAl2O4–Mg2TiO4 spinel solid solutions was studied. The XRD, XPS, and EDS results showed that Mg2TiO4 entered the lattice of MgAl2O4 to form a spinel solid solution, and the heterovalent substitution process was identified, where Ti4+ and Mg2+ ions of larger radius in the Mg2TiO4 replaced the Al3+ of smaller radius in the MgAl2O4. For the sample at x = 0.08, the spinel solid solutions exhibited the optimized densification with a relative density of 93.3%, an apparent porosity of 1.2%, and a compressive strength of 84.5 MPa. A significant increase in densification was related to the lattice distortion induced by ion size mismatch during the heterovalent substitution, thus accelerating the diffusion rate of Mg2+ and Al3+ ions in the spinelisation state. Moreover, the solid solubility content of Ti4+ in the MgAl2O4–Mg2TiO4 spinel solid solutions had a significant effect on the grain morphologies. The Mg2TiO4 heterogeneous nucleating agent significantly increased the spinelisation rate of MgAl2O4 spinel with negligible effect on densification.

Low-temperature synthesis of micro/nano Lithium Fluoride added magnesium aluminate spinel

Effect of Lif on the Optical Transmittance of Magnesium Aluminate Spinel

Synthesis of magnesium aluminate spinel by reaction sintering with different magnesia sources

Influence of LiF on the Infrared Transmissivity of Magnesia Alumina Spinel Transparent Ceramics

Microwave idrothermal synthesis of magnesium-aluminium spinel

In-situ Synthesized Mg-AL Spinel at Low Temperature Used Chloride Ion Mg-AL Hydrotalcites

Low-temperature densification of Mg2SnO4 ceramics with LiF-Fe2O3-V2O5 additive

Microstructure and Enhanced Magnetic Properties of Low-Temperature Sintered LiZnTiMn Ferrite Ceramics with Bi2O3-Al2O3 Additive

Self-Propagating High-Temperature Synthesis of Magnesium Aluminate Spinel Using Mg–Al Alloy

Sintering behavior and microstructure of (1-x)MgAl2O4-xMg2TiO4 spinel solid solutions prepared by isostructural heterogeneous nucleation

The low temperature fabrication of nanocrystalline MgAl2O4 spinel aerogel by a non-alkoxide sol-gel route

Effects of LiF on Crystal Structure, Cation Distributions and Microwave Dielectric Properties of MgAl2O4

Mechanism of in-situ formation of spinel and its effect on the mechanical properties of Al2O3–C refractories

A novel low thermal conductivity refractory aggregate for high-temperature applications: Lightweight microporous alumina-rich spinel (Mg0.4Al2.4O4)

Microstructure and Gyromagnetic Properties of Low-Sintered LiZnTi Ferrite Doped with Nano-Lizn and V2O5 Additives

Preparation of Magnesium Aluminate Spinel Nanofibers with High Temperature Resistance by Electrospinning Process Based on Non-Hydrolytic Sol-Gel Method

A strategy for controlling microstructure and mechanical properties of microporous spinel (MgAl2O4) aggregates from magnesite and Al(OH)3

Insight into the Growth Mechanism of Low-Temperature Synthesis of High-Purity Lithium Slag-Based Zeolite A

Synthesis of Highly Uniform and Compact Lithium Zinc Ferrite Ceramics via an Efficient Low Temperature Approach

Low Temperature Firing of Li0.43zn0.27ti0.13fe2.17o4 Ferrites with Enhanced Magnetic Properties

Polyol-mediated synthesis and characterization of magnesium–aluminum spinel nanoparticles