Abstract:Magnesium aluminate (MgAl2O4) spinel has grasped considerable attention in high-temperature application by right of its excellent properties. However, the poor sintering behavior of MgAl2O4 is detrimental to its further development. In the present work, the application of isostructural heterogeneous nucleation method provides a novel idea for optimizing the sintering behavior of refractory materials. A series of (1-x)MgAl2O4-xMg2TiO4 (x = 0, 0.02, 0.04, 0.06, 0.08, and 0.1) spinel solid solutions with a present ration of components were fabricated from light calcined magnesia, reactive alumina and pre-preparation Mg2TiO4. The effect of Mg2TiO4 heterogeneous nucleating agent on the crystalline phase, densification, and microstructure evolution of MgAl2O4–Mg2TiO4 spinel solid solutions was studied. The XRD, XPS, and EDS results showed that Mg2TiO4 entered the lattice of MgAl2O4 to form a spinel solid solution, and the heterovalent substitution process was identified, where Ti4+ and Mg2+ ions of larger radius in the Mg2TiO4 replaced the Al3+ of smaller radius in the MgAl2O4. For the sample at x = 0.08, the spinel solid solutions exhibited the optimized densification with a relative density of 93.3%, an apparent porosity of 1.2%, and a compressive strength of 84.5 MPa. A significant increase in densification was related to the lattice distortion induced by ion size mismatch during the heterovalent substitution, thus accelerating the diffusion rate of Mg2+ and Al3+ ions in the spinelisation state. Moreover, the solid solubility content of Ti4+ in the MgAl2O4–Mg2TiO4 spinel solid solutions had a significant effect on the grain morphologies. The Mg2TiO4 heterogeneous nucleating agent significantly increased the spinelisation rate of MgAl2O4 spinel with negligible effect on densification.

From layered double hydroxide to spinel nanostructures: facile synthesis and characterization of nanoplatelets and nanorods

Facile and green hydrothermal synthesis of MgAl/NiAl/ZnAl layered double hydroxide nanosheets: a physiochemical comparison

Microwave idrothermal synthesis of magnesium-aluminium spinel

Self-Propagating High-Temperature Synthesis of Magnesium Aluminate Spinel Using Mg–Al Alloy

Polyol-mediated synthesis and characterization of magnesium–aluminum spinel nanoparticles

Syntheses of Nanocrystalline Mg-Al-LDHs and PO_4~(3-), P_2O_7~(4-) Anion-Pillared Layered Double Hydroxides under the Conditions of Microwave

Hydrothermal Synthesis of Layered Double Hydroxides (ldhs) from Mixed MgO and Al2O3: LDH Formation Mechanism

Nano-size MZnAl (m=cu, Co, Ni) Metal Oxides Obtained by Combining Hydrothermal Synthesis with Urea Homogeneous Precipitation Procedures

Synthesis and Characterization of Porous Magnesium Aluminate Spinel by Hydrothermal Process

Simple Synthesis of Single-crystalline Nanoplates of Magnesium Oxide

Efficient, scalable, closed-loop synthesis of highly crystalline pure phase MgAl-layered double hydroxides intercalated with hydroxyl anions

Structural, morphological, and magnetic studies of spinel ferrites derived from layered double hydroxides

Dispersion and Size Control of Layered Double Hydroxide Nanoparticles in Aqueous Solutions

Novel Synthesis of High Surface Area MgAl2O4 Spinel As Catalyst Support

Effect of Synthetic Parameters on Synthesis of Magnesium Aluminum Spinels

A Green Route for the Preparation of Layered Double Hydroxides from Basic Magnesium Carbonate

Hydrolysis Process and Mechanism of Magnesium Aluminate Alkoxides

A Simple Hydrothermal Method to Synthesise Highly Pure Hexagonal and Rhombus Alpha-Lialo2 Nanosheets

Formation of rod-like Mg(OH)2 nanocrystallites under hydrothermal conditions and the conversion to MgO nanorods by thermal dehydration

Synthesis, Electronic Structure, and Electrochemical Properties of the Cubic Mg2MnO4 Spinel with Porous-Spongy Structure

Sintering behavior and microstructure of (1-x)MgAl2O4-xMg2TiO4 spinel solid solutions prepared by isostructural heterogeneous nucleation