Preparation and electrochemical properties of Ni–La2-xMgxCe2O7- hydrogen-separation membrane
Qingtao Shen,Chunli Yang,Weiji Cao,Jun Li,Lei Wang,Wei Yao,Yanru Liang,Kai Wang,Sining Yun
DOI: https://doi.org/10.1016/j.ceramint.2023.09.323
IF: 5.532
2023-09-01
Ceramics International
Abstract:Oxides with a fluorite structure, such as La2Ce2O7, show robust resistance to H2O and CO2, making them an increasingly favored material for proton conduction. This study explored the impact of Mg doping on the electrochemical properties of La2Ce2O7 materials. The experimental findings demonstrated that the La2-x Mg x Ce2O7-δ sample with x = 0.15 produced the greatest conductivity. As a result of its proportional link with proton conductivity, this led to the Ni–La1.85Mg0.15Ce2O7-δ membrane with the greatest hydrogen penetration flux. As the membrane thickness was large, the hydrogen permeation process was primarily governed by bulk diffusion. When the thickness fell below 0.54 mm, surface diffusion began to control the hydrogen permeation process. Surface modification with Pt and Ni significantly enhanced the hydrogen permeability of the membrane. Moreover, Ni–La2-xMgxCe2O7-δ membranes with diverse Mg contents exhibited good stability in a humid atmosphere with 20% CO2.
materials science, ceramics