Mechanical Property and Fracture Characteristic of Induction Brazed Joints of TiAl-based Intermetallics to Steel 35crmo with Ag–Cu–Ni–Li Filler

P He,JC Feng,W Xu

DOI: https://doi.org/10.1016/j.msea.2005.08.147

IF: 6.044

2005-01-01

Materials Science and Engineering A

Abstract:TiAl-based intermetallics joined by vacuum induction brazing using Ag–Cu–Ni–Li filler at 850–970°C for 1–10min was investigated. The interfacial microstructure and strength of the brazed joints were comprehensively evaluated, and the optimum brazing parameters were obtained. Comparing the high-temperature–short time conditions and the low temperature–longtime conditions, the interfacial microstructure under high-temperature–short time conditions is more appropriate, whose interfacial microstructure is mostly non-equilibrium crystal, and it has fine mechanical properties. The optimum brazing parameters are as follows: brazing temperature is 920–930°C, brazing time is 1–2min, the largest tensile strength is 324MPa.