Abstract:Binary Mg–Ca alloys with various Ca contents were fabricated under different working conditions. X-ray diffraction (XRD) analysis and optical microscopy observations showed that Mg–xCa (x=1–3 wt%) alloys were composed of two phases, α(Mg) and Mg2Ca. The results of tensile tests and in vitro corrosion tests indicated that the mechanical properties could be adjusted by controlling the Ca content and processing treatment. The yield strength (YS), ultimate tensile strength (UTS) and elongation decreased with increasing Ca content. The UTS and elongation of as-cast Mg–1Ca alloy (71.38±3.01MPa and 1.87±0.14%) were largely improved after hot rolling (166.7±3.01MPa and 3±0.78%) and hot extrusion (239.63±7.21MPa and 10.63±0.64%). The in vitro corrosion test in simulated body fluid (SBF) indicated that the microstructure and working history of Mg–xCa alloys strongly affected their corrosion behaviors. An increasing content of Mg2Ca phase led to a higher corrosion rate whereas hot rolling and hot extrusion could reduce it. The cytotoxicity evaluation using L-929 cells revealed that Mg–1Ca alloy did not induce toxicity to cells, and the viability of cells for Mg–1Ca alloy extraction medium was better than that of control. Moreover, Mg–1Ca alloy pins, with commercial pure Ti pins as control, were implanted into the left and right rabbit femoral shafts, respectively, and observed for 1, 2 and 3 months. High activity of osteoblast and osteocytes were observed around the Mg–1Ca alloy pins as shown by hematoxylin and eosin stained tissue sections. Radiographic examination revealed that the Mg–1Ca alloy pins gradually degraded in vivo within 90 days and the newly formed bone was clearly seen at month 3. Both the in vitro and in vivo corrosion suggested that a mixture of Mg(OH)2 and hydroxyapatite formed on the surface of Mg–1Ca alloy with the extension of immersion/implantation time. In addition, no significant difference (p>0.05) of serum magnesium was detected at different degradation stages. All these results revealed that Mg–1Ca alloy had the acceptable biocompatibility as a new kind of biodegradable implant material. Based on the above results, a solid alloy/liquid solution interface model was also proposed to interpret the biocorrosion process and the associated hydroxyapatite mineralization.

Microstructure, Biocorrosion And Cytotoxicity Evaluations Of Rapid Solidified Mg-3ca Alloy Ribbons As A Biodegradable Material

Development of Biocompatible Bulk MgZnCa Metallic Glass with Very High Corrosion Resistance in Simulated Body Fluid

In Vitro Degradation and Biocompatibility of Mg-Li-Ca Alloys—the Influence of Li Content

Microstructure, Mechanical Properties, Corrosion Behavior and Biocompatibility of As-Extruded Biodegradable Mg–3Sn–1Zn–0.5Mn Alloy

Corrosion Resistance and Surface Biocompatibility of a Microarc Oxidation Coating on a Mg–Ca Alloy

Microstructure, mechanical properties, and in vitro behavior of biodegradable Zn-1Mg-0.1Ca and Zn-1Mg-0.5Ca

The Development of Binary Mg-Ca Alloys for Use As Biodegradable Materials Within Bone

Microstructure, Mechanical Properties, in Vitro Degradation and Cytotoxicity Evaluations of Mg–1.5Y–1.2Zn–0.44Zr Alloys for Biodegradable Metallic Implants

Biocorrosion and Cytotoxicity Studies on Biodegradable Mg-Based Multicomponent Alloys

Microstructure, Mechanical and Corrosion Properties and Biocompatibility of Mg-Y-Zn-Zr Rolled Alloy for Biomedical Applications

Microstructure, texture, and mechanical properties of Mg–4Zn–1Mn–xCa alloys and the fabrication of biomedical Mg thin-walled micro-tubes

In Vitro Degradation Performance and Biological Response of a Mg–Zn–Zr Alloy

Microstructure, anticorrosion, biocompatibility and antibacterial activities of extruded Mg−Zn−Mn strengthened with Ca

A homogenous microstructural Mg-based matrix model for orthopedic application with generating uniform and smooth corrosion product layer in Ringer's solution: Study on biodegradable behavior of Mg-Zn alloys prepared by powder metallurgy as a case

Investigating the mechanical properties and corrosion resistance of extruded Mg-1Zn-xCaO (x=0, 0.5, 1.0 wt%) materials

In vivo performance of a rare earth free Mg-Zn-Ca alloy manufactured using twin roll casting for potential applications in the cranial and maxillofacial fixation devices

Effects of Inorganic Ions, Organic Particles, Blood Cells, and Cyclic Loading on in Vitro Corrosion of Mg Al Alloys

Novel Mg-Al-Sn-Ca with enhanced mechanical properties and high corrosion rate via sub-rapid solidification for degradable magnesium alloy

In Vitro Corrosion and Cytocompatibility of A Microarc Oxidation Coating and Poly(L-Lactic Acid) Composite Coating on Mg-1li-1ca Alloy for Orthopedic Implants

Microstructure and In Vitro Evaluation of Extruded and Hot Drawn Alloy MgCa0.7 for Biodegradable Surgical Wires

In Vitro Corrosion of Mg–1.21Li–1.12Ca–1Y Alloy