Abstract:Binary Mg–Ca alloys with various Ca contents were fabricated under different working conditions. X-ray diffraction (XRD) analysis and optical microscopy observations showed that Mg–xCa (x=1–3 wt%) alloys were composed of two phases, α(Mg) and Mg2Ca. The results of tensile tests and in vitro corrosion tests indicated that the mechanical properties could be adjusted by controlling the Ca content and processing treatment. The yield strength (YS), ultimate tensile strength (UTS) and elongation decreased with increasing Ca content. The UTS and elongation of as-cast Mg–1Ca alloy (71.38±3.01MPa and 1.87±0.14%) were largely improved after hot rolling (166.7±3.01MPa and 3±0.78%) and hot extrusion (239.63±7.21MPa and 10.63±0.64%). The in vitro corrosion test in simulated body fluid (SBF) indicated that the microstructure and working history of Mg–xCa alloys strongly affected their corrosion behaviors. An increasing content of Mg2Ca phase led to a higher corrosion rate whereas hot rolling and hot extrusion could reduce it. The cytotoxicity evaluation using L-929 cells revealed that Mg–1Ca alloy did not induce toxicity to cells, and the viability of cells for Mg–1Ca alloy extraction medium was better than that of control. Moreover, Mg–1Ca alloy pins, with commercial pure Ti pins as control, were implanted into the left and right rabbit femoral shafts, respectively, and observed for 1, 2 and 3 months. High activity of osteoblast and osteocytes were observed around the Mg–1Ca alloy pins as shown by hematoxylin and eosin stained tissue sections. Radiographic examination revealed that the Mg–1Ca alloy pins gradually degraded in vivo within 90 days and the newly formed bone was clearly seen at month 3. Both the in vitro and in vivo corrosion suggested that a mixture of Mg(OH)2 and hydroxyapatite formed on the surface of Mg–1Ca alloy with the extension of immersion/implantation time. In addition, no significant difference (p>0.05) of serum magnesium was detected at different degradation stages. All these results revealed that Mg–1Ca alloy had the acceptable biocompatibility as a new kind of biodegradable implant material. Based on the above results, a solid alloy/liquid solution interface model was also proposed to interpret the biocorrosion process and the associated hydroxyapatite mineralization.

Attosecond control of dissociative ionization of O(2) molecules

Microstructure, Mechanical Properties, and in Vitro Corrosion Behavior of Biodegradable Zn-1Fe-xMg Alloy

Design and characterizations of novel biodegradable Zn-Cu-Mg alloys for potential biodegradable implants

Microstructure, Mechanical Properties, in Vitro Degradation and Cytotoxicity Evaluations of Mg–1.5Y–1.2Zn–0.44Zr Alloys for Biodegradable Metallic Implants

Effects of alloying elements (Ca and Sr) on microstructure, mechanical property and in vitro corrosion behavior of biodegradable Zn-1.5Mg alloy

Microstructure, Mechanical Properties, Corrosion Behavior and Biocompatibility of As-Extruded Biodegradable Mg–3Sn–1Zn–0.5Mn Alloy

Microstructure, mechanical properties, in vitro degradation behavior and hemocompatibility of novel Zn–Mg–Sr alloys as biodegradable metals

Development of biodegradable Zn-1X binary alloys with nutrient alloying elements Mg, Ca and Sr

Microstructure, anticorrosion, biocompatibility and antibacterial activities of extruded Mg−Zn−Mn strengthened with Ca

Micro-alloying with Mn in Zn–Mg alloy for future biodegradable metals application

Investigating the mechanical properties and corrosion resistance of extruded Mg-1Zn-xCaO (x=0, 0.5, 1.0 wt%) materials

Effects of Ag, Cu or Fe addition on microstructure and comprehensive properties of biodegradable Zn-Mg alloy

Evaluation on the corrosion resistance, antibacterial property and osteogenic activity of biodegradable Mg-Ca and Mg-Ca-Zn-Ag alloys

In Vitro and in Vivo Studies on As-Extruded Mg- 5.25Wt.%zn-0.6Wt.%ca Alloy As Biodegradable Metal

Fabrication and Properties of a Biodegradable Zn-Ca Composite

Design and characterizations of novel biodegradable ternary Zn-based alloys with IIA nutrient alloying elements Mg, Ca and Sr

Corrosion behavior, antibacterial properties and in vitro and in vivo biocompatibility of biodegradable Zn-5Cu-xMg alloy for bone-implant applications

The Development of Binary Mg-Ca Alloys for Use As Biodegradable Materials Within Bone

Don't ignore the right radial approach.

Enhanced Mechanical Properties, Corrosion Resistance, Cytocompatibility, Osteogenesis, and Antibacterial Performance of Biodegradable Mg‐2Zn‐0.5Ca‐0.5Sr/Zr Alloys for Bone‐Implant Application

Influence of Zirconium (Zr) on the microstructure, mechanical properties and corrosion behavior of biodegradable zinc-magnesium alloys