Effects of Ag, Cu or Fe addition on microstructure and comprehensive properties of biodegradable Zn-Mg alloy

Madeeha Riaz,Saba Shahzadi,Hina Imtiaz,Tousif Hussain

DOI: https://doi.org/10.1016/j.mtcomm.2024.108513

IF: 3.8

2024-03-04

Materials Today Communications

Abstract:In recent years, Zn-0.5 wt.%Mg alloys have drawn a lot of attention as a potential candidate in biodegradable implant applications as it demonstrated more corrosion resistant property in comparison to Fe- and Mg-based alloys. Zn-0.5 wt%Mg based alloys were fabricated through powder metallurgy. This work examined the impact of the micro-alloying metals Cu, Fe, and Ag on Zn-Mg alloys. Moreover, the structure, absorbing properties, morphology, electrochemical properties, electrical properties, and wettability were also investigated. All fabricated Zn-0.5 wt%Mg alloys formed a primary phase of Mg 2 Zn 11 and secondary phase of MgZn 2 . A minor phase of Zn was also identified in XRD analysis. Optical analysis showed that the Zn-0.5 wt.%Mg-0.2 wt.%Cu alloy gave a strong peak of absorbance at a short wavelength of 230 nm which is due to its colour. All alloys sintered at 350 ◦C displayed micro-needles having size in the range of 1.82-26.2 μm in SEM analysis. Zn-0.5 wt.% Mg-0.2 wt.% Cu alloy offered 140 Hv value of Vickers hardness. The electrochemical test findings measured corrosion resistance and most corrosion resistant material was Zn-0.5 wt.%Mg-0.2 wt.%Cu alloy with corrosion rate 0.0120 mm/year. Zn-0.5 wt%Mg-0.2 wt%Cu offered the conductivity with the least value of 7.45 ×10 -12 Ω -1 m -1 and highest value of resistivity at 1.335 ×10 11 Ω-m, based on electrochemical study. All fabricated biodegradable Zn-0.5 wt.%Mg alloys had an angle less than 90, indicating hydrophilicity as determined by wettability studies. Zn-0.5 wt.%Mg-0.2 wt.%Cu is the most suitable alloy in cardiovascular stent and orthopaedic implant applications.

materials science, multidisciplinary