Abstract:Microarc oxidation (MAO) was used to prepare a TiO2-based coating containing Ca and P on titanium alloy. An alkali treatment was developed to modify the surface of the MAO coating to improve the apatite-forming ability of the coating. The chemically treated MAO coating exhibits a modified layer, with the main constituents being O, Ti, Ca and Na, showing anatase. The modified MAO coating shows a rough and porous morphology containing numerous nanoflakes of ∼100nm thickness. During the alkali treatment process, P on the surface of the MAO coating shows a main dynamic process of dissolution; however, Ca exhibits a re-deposition process as well as dissolution. The formation of the modified layer could be explained by this mechanism: negatively charged HTiO3- ions are formed on the MAO coating due to the attack of OH− ions on the TiO2 phase. The HTiO3- ions could incorporate sodium from the alkali solution and calcium from the alkali solution and MAO coating. The apatite-forming ability of the MAO coating is improved remarkably by the simple chemical treatment, since the surface of the alkali-treated MAO coating could provide abundant Ti–OH groups probably formed by ionic exchanges between (Ca2+, Na+) ions of the alkali-treated MAO coating and H3O+ ions of a simulated body fluid (SBF). Moreover, Ca released from the alkali-treated MAO coating increases the degree of supersaturation of SBF, promoting the formation of apatite. The apatite induced by the alkali-treated MAO coating possesses carbonated structure and pore networks on the nanometer scale.

Biomimetic Apatite Deposited on Microarc Oxidized Anatase-Based Ceramic Coating

Biomimetic Deposition of Apatite on Electrochemically Oxidized Titanium Substrates

Apatite deposition on thermally and anodically oxidized titanium surfaces in a simulated body fluid.

[Experimental Study of Fast Formation of Biomimetic Apatite Coatings on Pure Titanium Surface].

Structure, cell response and biomimetic apatite induction of gradient TiO2-based/nano-scale hydrophilic amorphous titanium oxide containing Ca composite coatings before and after crystallization.

Biomimetic Apatite Coatings on Micro-Arc Oxidized Titania

Formation Mechanism of Biomedical Apatite Coatings on Porous Titania Layer

[Fast Formation of Biomimetic Apatite Coatings on Pure Porous Titanium Implant's Surface].

Biomimetic Deposition of Apatite Coatings on Biomedical Niti Alloy Coated with Amorphous Titanium Oxide by Microarc Oxidation

Effects of Structure and Composition of the CaP Composite Coatings on Apatite Formation and Bioactivity in Simulated Body Fluid

Characteristic and in vitro bioactivity of a microarc-oxidized TiO2-based coating after chemical treatment

Longer-Term Mechanical And Biological Evaluation Of Titanium Alloy Coated With Apatite Layer

The structure and in vitro apatite formation ability of porous titanium covered bioactive microarc oxidized TiO2-based coatings containing Si, Na and Ca

Transformation of nacre coatings into apatite coatings in phosphate buffer solution at low temperature.

Biomimetic Deposition of Apatite Coatings on Micro-Arc Oxidation Treated Biomedical NiTi Alloy

In Simulated Body Fluid Performance of Polymorphic Apatite Coatings Synthesized by Pulsed Electrodeposition

Formation of apatite on porous titanium in different supersaturated calcification solution

In vitro apatite formation on porous anodic alumina induced by a phosphorylation treatment

Preparation, Cell Response and Apatite-Forming Ability of Microarc Oxidized Coatings Containing Si, Ca and Na on Titanium

The Influence of Surface Morphology of Dense Ca-P Ceramics on Apatite Formation in Dynamic SBF

Effect of heat treatment on the structure and in vitro bioactivity of microarc-oxidized (MAO) titania coatings containing Ca and P ions