Abstract:For development of thin bioactive coatings on metal implants, a dense and uniform apatite layer was coated onto titanium (Ti) implants in situ by using a new biomimetic method, which is composed of apatite nucleation and growth steps in simulated body fluid (SBF). Analysis of the coatings by thin film X-ray diffraction and scanning electron microscopy-energy dispersive X-ray microanalysis (SEM-EMPA) before implantation showed that its characteristics were very similar to those of natural bone. The coated and uncoated rectangular plates were bilaterally implanted into the tibial proximal metaphyses of rabbits. After 6, 10 and 25 weeks post-implantation, the bone bonding and bone formation at the bone-implant interfaces were evaluated by a detachment test and undecalcified histological examination. Mechanical testing in tension showed that the failure load of apatite layer-coated Ti implants was significantly higher than that of uncoated control at each time period (all P < 0.001). Histologically, it was shown that bone was deposited directly onto the apatite coating without any intervening soft tissue, while in the paired controls, interpositional soft tissue was seen at the bone-implant interface. By SEM-EPMA, a uniform calcium- and phosphorus-rich layer was detected between the coated implants and bone, but not in uncoated controls at either earlier or later time periods. The results indicate that the apatite layer deposited on Ti in situ may significantly increase the bone bonding strength by providing a bioactive surface, which allows for an early bone apposition to the implant. In addition, the apatite layer-coated Ti produced by the biomimetic process may fulfil the requirements of favourable thin coatings and strong adhesion at the metal-coating interface.

Relationship between Vitamin D Levels and Depressive Symptoms in Renal Transplant Recipients

Apatite deposition on thermally and anodically oxidized titanium surfaces in a simulated body fluid.

Biomimetic Deposition of Apatite on Electrochemically Oxidized Titanium Substrates

A Comparative Study of in Vitro Apatite Deposition on Heat-, H2O2-, and NaOH-treated Titanium Surfaces

Synthesis and characterization of silver substituted strontium phosphate silicate apatite using solid-state reaction for osteoregenerative applications

Longer-Term Mechanical And Biological Evaluation Of Titanium Alloy Coated With Apatite Layer

Osteoblast Responses to Thin Nanohydroxyapatite Coated on Roughened Titanium Surfaces Deposited by an Electrochemical Process.

Apatite Layer-Coated Titanium for Use As Bone Bonding Implants

[Fast Formation of Biomimetic Apatite Coatings on Pure Porous Titanium Implant's Surface].

Surface Phosphonation Treatment Shows Dose-Dependent Enhancement of the Bioactivity of Polyetheretherketone

Stabilization of Apatite Coatings on PPENK Surfaces by Mechanical Interlocking to Promote Bioactivity and Osseointegration In Vivo

I-Bit Differential Detection of GMSK with Data-Aided Phase Control

Surface phosphonation treatment shows dose-dependent enhancement of the bioactivity of polyetheretherketone (vol 9, pg 30076, 2019)

Surface Modification of Carbon Fiber-Polyetheretherketone Composite to Impart Bioactivity by Using Apatite Nuclei

Rapid structural evolution and bone inducing mechanism of the multilayer coating with silicon-doped hydroxyapatite crystals on the microwave water steaming-hydrothermally treated titania coating

Micro/Nanoscale Surface Modification of Ti6Al4V Alloy for Implant Applications

In vitro bioactive behavior of hydroxylapatite-coated porous Al(2)O(3)

Formation of Bone-Like Apatite on Poly(l-Lactide) to Improve Osteoblast-Like Compatibility in Vitro and in Vivo

Biomimetic Deposition of Apatite on Surface Chemically Modified Porous Niti Shapememory Alloy

Apatite Formation on α-Tricalcium Phosphate Modified with Bioresponsive Ceramics in Simulated Body Fluid Containing Alkaline Phosphatase

On the way to increase osseointegration potential: Sequential SI-ATRP as promising tool for PEEK-based implant nano-engineering