Abstract:Arrays of randomly oriented zinc oxide (ZnO) nanowires were fabricated on silicon wafers via a simple thermal evaporation method. During the fabrication, the temperature around the substrate was below 500°C. The products were analyzed by conventional means and determined to be single crystals of wurtzite-type ZnO that grew along the c-axis. These nanowires were 10–100nm in diameter and 10–100μm in length, suggesting a possible high field enhancement factor. The dependence of the field emission current on the anode–cathode voltage (I–V behavior) of the ZnO nanowire arrays was measured in a lab-built ultrahigh vacuum system with a base pressure of 10−7Pa. After surface cleaning by heat treatment, two characteristic electric fields, under which 10μA/cm2 and 1mA/cm2 current densities were extracted, were measured to be 4.0 and 4.7V/μm, respectively. As observed with a transparent anode, emission occurred uniformly over the whole sample surface. A 72h-long test on emission stability was performed under a constant voltage of 2.75kV. The current dropped occasionally to approximately 80% of the initial value during the test owing to the poor adherence of the nanowires to the substrate. These preliminary results have shown the perspective of, as well as a major drawback to, a ZnO nanowire array being developed into a cold electron source to be used in future electronic devices.

High‐Density, Ordered Ultraviolet Light‐Emitting ZnO Nanowire Arrays

Ordered nanowire array blue/near-UV light emitting diodes.

Vapor phase growth and photoluminescence of oriented-attachment Zn2GeO4 nanorods array

Photoluminescence Characterization of Nanocrystalline ZnO Array

Ultraviolet-Emitting Zno Nanowires Synthesized By A Physical Vapor Deposition Approach

Phosphorus Doped Zn(1-x)Mg(x)O Nanowire Arrays.

Preparation and Photoluminescence Properties of ZnO Nanowire/Nanorod Mix Arrays

Layer-structured ZnO Nanowire Arrays with Dominant Surface- and Acceptor-Related Emissions

Photoluminescence and Low-Threshold Lasing of ZnO Nanorod Arrays.

Aligned growth of ZnO nanowires and lasing in single ZnO nanowire optical cavities

Ultraviolet Lasing and Time-Resolved Photoluminescence of Well-Aligned ZnO Nanorod Arrays

Arrays of ZnO Nanowires Fabricated by a Simple Chemical Solution Route

Aligned growth of ZnO nanowires by NAPLD and their optical characterizations

Fabrication, Characterization and Field Emission Properties of Large-Scale Uniform ZnO Nanotube Arrays.

Fabrication of Large-Area ZnO Nanowire Field Emitter Arrays by Thermal Oxidation for High-Current Application

Photoluminescence and Lasing Properties of Catalyst-Free ZnO Nanorod Arrays Fabricated by Pulsed Laser Deposition

Field Emission from Nonaligned Zinc Oxide Nanowires

Field Emission and Optical Properties of ZnO Nanowires Grown Directly on Conducting Brass Substrates.

Aligned Growth of ZnO Nanowires by Laser Ablation and Their Applications

Density-Controlled Growth of Zno Nanowires Via Nanoparticle-Assisted Pulsed-Laser Deposition and Their Optical Properties

Field Emission Properties of Zinc Oxide Nanowires Fabricated by Thermal Evaporation