Abstract:Geopolymer is a potential substitute for high-emission cement production . Therefore, the use of fly ash with high emission as a geopolymer is an environmentally friendly and inexpensive direction. However, fly ash (FA) is a high amorphous precursor with low pozzolanic reactivity making it difficult to be activated by calcium hydroxide. In this study, the coupling of wet-milling mechanical force and calcium hydroxide was used to prepare high-performance alkaline calcium activated geopolymers. Two kinds of FA slurries with different particle sizes of D 50 = 2.96 μm and 14.2 μm were prepared, activated by calcium hydroxide (CH) with the content of 4%, 11% and 19%. Results indicated that the increase of calcium hydroxide content was beneficial to developing strength, effectively improving the chloride resistance, compacting the microstructure, but increasing the autogenous shrinkage of the geopolymers. These improvements are especially apparent in the wet-milled fly ash geopolymers (WFA) due to the pre-depolymerization implemented by wet-milled mechanical forces, and coupled with the activation effect of CH to improve the depolymerization efficiency and condensation reaction. The compressive strength of WF-CH-19 was three times higher than that of FA-CH-19, reaching 29.3 MPa at 28 d, and the compressive strength growth of WF-CH-11 even reached 591.67% at 1 d. Meanwhile, the main chain length (MCL) and Al/Si of calcium silicate hydrates were clearly improved, and pore structure was significantly refined with capillary pore increased from 29.79% to 89.23%. In addition, FA and WFA geopolymers have significant advantages over Portland cement in the environmental impact indicators such as E-energy and E-CO 2 .

Dissolution and Geopolymerization Mechanism and Performances of Fly Ash Geopolymer

Synthesis and Properties of Fly Ash Geopolymer with Dyeing Sludge

Strength and microstructure of class C fly ash based geopolymer activated with sodium silicate powder

Properties of geopolymer based on fly ash

Mechanism of Polymerization During the Solidification of Flyash-based Geopolymers

Study on the Geopolymer Based on Fly Ash and Slag

Solidification and Immobilization of MSWI Fly Ash Through Aluminate Geopolymerization: Based on Partial Charge Model Analysis.

Impacts of Alkaline Washing Pretreatment on Municipal Solid Waste Incineration Fly Ash (MSWI FA) and Resulting Geopolymers

Research on Resource Utilization of Dyeing Sludge with High Calcium Fly Ash

Study on Fabrication and Microstructures of Fly Ash Based Geopolymeric Cements

Utilization of Calcium Carbide Residue as Solid Alkali for Preparing Fly Ash-Based Geopolymers: Dependence of Compressive Strength and Microstructure on Calcium Carbide Residue, Water Content and Curing Temperature

The effects of alkaline dosage and Si/Al ratio on the immobilization of heavy metals in municipal solid waste incineration fly ash-based geopolymer.

The Composition of Fly Ash Glass Phase and Its Dissolution Properties Applying to Geopolymeric Materials

The influence of calcium content on the structure and thermal performance of fly ash based geopolymers

Performances and microstructure of one-part fly ash geopolymer activated by calcium carbide slag and sodium metasilicate powder

Microstructure, Compressive Strength and Sound Insulation Property of Fly Ash-Based Geopolymeric Foams with Silica Fume as Foaming Agent

An efficient approach for sustainable fly ash geopolymer by coupled activation of wet-milling mechanical force and calcium hydroxide

Mechanical behavior and microstructure evolution of slag-fly ash based geopolymer stabilized sand

Study of Manufacture Process and Properties of Fly Ash-Based Geopolymers

Feasibility analysis of the preparation of geopolymers from different types of coal based ash: Reaction, synthesis, and properties

Low-carbon wet-ground fly ash geopolymer activated by single calcium carbide slag