Abstract:In this study, a yttria-stabilized zirconia (YSZ) ceramic matrix abradable sealing coating named 8YSZ-5 was successfully prepared by mixed solution precursor plasma spraying, and its thermal shock behavior was studied in detail. During the thermal shock cycles, the microstructure, residual stress and phase stability of the 8YSZ-5 coating were examined by using scanning electron microscopy (SEM), transmission electron microscopy (TEM) and X-ray diffraction (XRD) technique. The results show that the 8YSZ-5 coating has excellent thermal shock resistance through a 200-cycle thermal shock test at 1150 degrees C. During the thermal shock cycles, the spallation only existed in a small scale in the edge of the 8YSZ-5 coating, and the coating always maintains a stable phase composition of tetragonal structure. The residual stress study shows that the in-plane residual stress of the 8YSZ-5 coating is detected to be compressive stress, which increases with increasing the thermal shock cycles. The microstructure analysis shows that as the thermal shock test progresses, the number of the pores in the coating gradually decreases due to their spontaneous closure and the average size of the grains gradually increases. The mechanical properties investigation shows that the hardness and surface friction coefficient of the 8YSZ-5 abradable sealing coating increase gradually, while the bond strength of the coating decreases by 50% after 200 thermal shock cycles. The implications of this study are important for the design of advanced abradable sealing coatings prepared by the mixed solution precursor plasma spraying technology.

Agglomeration on Drying of Yttria-Stabilised-zirconia Slurry on a Metal Substrate

Fabrication and Characterization of Y2O3 Stabilized ZrO2 Films Deposited with Aerosol-Assisted MOCVD

Formation and Rate Processes of Y[sub 2]o[sub 3] Stabilized ZrO[sub 2] Thin Films from Zr(DPM)[sub 4] and Y(DPM)[sub 3] by Cold-Wall Aerosol-Assisted MOCVD

Formation and Rate Processes of Y2o3 Stabilized Zro2 Thin Films from Zr(Dpm)(4) and Y(Dpm)(3) by Cold-Wall Aerosol-Assisted Mocvd

Polymeric Adsorption Behavior of Nanoparticulate Yttria Stabilized Zirconia and the Deposition of As-Formed Suspensions on Dense Α-Al2o3 Substrates

Influence of Substrate Temperature on Microcracks Formation in Plasma-Sprayed Yttria-Stabilized Zirconia Splats

Dispersion and Stability of 8 Mol.% Yttria Stabilized Zirconia Suspensions for Dip-Coating Filtration Membranes

Characterisation of Ceramic Coatings Sintering Using Residual Stress Measurements

Preparation and Characterization of YSZ Abradable Sealing Coating Through Mixed Solution Precursor Plasma Spraying

Wet-Milling Effect on the Properties of Ultrafine Yttria-Stabilized Zirconia Powders

Analysis of thermal shock performance of Y2O3 stabilized ZrO2 (YSZ) coating based on residual stress and micro-morphology

Experimental Simulation Study of Intersplat Bonding Formation by Deposition of YSZ Splats on Preheated YSZ Substrate

Study on Thermal Shock Behavior of YSZ Abradable Sealing Coating Prepared by Mixed Solution Precursor Plasma Spraying

Effect of spraying power on the morphology of YSZ splat and micro-structure of thermal barrier coating

EBSD analysis of microstructure changes in YSZ coatings during thermal cycling

Microstructure Evolution in Yttria Stabilized Zirconia During Laser Hybrid Induction Modification

Degradation of zirconia in moisture

Relationship between microstructure and bonding strength of yttria-stabilized zirconia thermal barrier coatings

Low Temperature Degradation of Yttria Stabilized Zirconia

Tailoring Wear and Tribo-Induced Interaction of YSZ Coating Sliding Against Si3N4 and Al2O3 Counterparts

Epitaxial growth and cracking of highly tough 7YSZ splats by thermal spray technology