Preparation and Characterization of Polybutylene Terephthalate/ Polymethyl Methacrylate Ammonium Salts Modified Montmorillonite Nanocomposites

Xiaoling HUANG,Xiaoli WANG,Bingbing ZHANG,Haiquan SU
DOI: https://doi.org/10.16085/j.issn.1000-6613.2011.05.032
2011-01-01
Abstract:Two polymethyl methacrylate ammonium salts(MAPS-B and MAPS-O)were used to modify montmorillonite.Such thermally stable oligomerically modified montmorillonites were further melt-compounded with polybutylene terephthalate(PBT)at a high temperature and six kinds of nanocomposites(PBT/MAPS-B-1,PBT/MAPS-B-2,PBT/MAPS-B-3,PBT/MAPS-O-1,PBT/MAPS-O-2 and PBT/MAPS-O-3)were obtained.The influence of the structure and content of oligomerically modified montmorillonite on the morphology and properties of the nanocomposites were evaluated.The results of X-ray diffraction(XRD)and transmission electrical microscopy(TEM)indicated that the PBT/MMT nanocomposites had intercalated structures.Increased clay loading was a disadvantage for clay dispersion in the polymer matrix.Thermogravimetric analysis(TGA)showed that thermal stabilities of the PBT/MAPS-B and PBT/MAPS-O nanocomposites were improved remarkably.The onset temperature of thermal degradation(Tonset)of PBT/MAPS-O-2 was 20 ℃ higher than that of the pristine material.The thermal stability of the composites was influenced by the dispersity of clay.The poor dispersity with clay loading higher than 2% resulted in decreased Tonset of PBT/MMT.The effects of modified clays on the crystallization behavior of PBT were characterized by differential scanning calorimeter(DSC).The results showed that the nanocomposites of polyester/MMT had higher crystallization rate and a little lower melting temperature than the pristine polyester.The crystallization rate increased with increasing MMT content.
What problem does this paper attempt to address?