Production for High Thermal Stability NdFeB Magnets

L. Q. Yu,J. Zhang,S. Q. Hu,Z. D. Han,M. Yan

DOI: https://doi.org/10.1016/j.jmmm.2007.11.022

IF: 3.097

2007-01-01

Journal of Magnetism and Magnetic Materials

Abstract:To improve sintered NdFeB magnets’ thermal stability and magnetic properties, combined addition of elements Cu and Gd was investigated. It was found that with Gd addition increase to 1.0%, the temperature coefficient α improved from −0.15 to −0.05%/°C (maximum working temperature 120°C), but the remanence and the maximum energy product linearly decreased. With addition of Cu in Gd-containing magnets the intrinsic coercivity increased greatly, and the remanence increased also because of their density improvement, and optimum Cu content was achieved at 0.2%. Microstructure analysis showed that most of the Cu distributed at grain boundaries and led to clear and smooth morphologies. Magnets with high thermal stability α=−0.05%/°C and magnetic properties were obtained with addition of Gd=0.8% and Cu=0.2%.