Grain boundary engineering towards high-figure-of-merit Nd-Ce-Fe-B sintered magnets: Synergetic effects of (Nd, Pr)Hx and Cu co-dopants
Jiaying Jin,Mi Yan,Wang Chen,Wenying Zhang,Zhiheng Zhang,Lizhong Zhao,Guohua Bai,Jean-Marc Greneche
DOI: https://doi.org/10.1016/j.actamat.2020.116529
IF: 9.4
2021-02-01
Acta Materialia
Abstract:<p>We present a potent pathway, (Nd, Pr)H<sub>x</sub> and Cu grain boundary engineering, to tackle the trade-offs between coercivity, remanence and corrosion resistance of Nd-Ce-Fe-B sintered magnets. Concurrent improvements of magnetic and corrosive properties are achieved in 25 wt% Ce-substituted magnet depending on the (Nd, Pr)H<sub>x</sub>/Cu ratio. A representative 8:2 ratio yields room-temperature magnetic performance (<em>H</em><sub>cj</sub> = 14.1 kOe, <em>B</em><sub>r</sub> = 12.88 kG, (<em>BH</em>)<sub>max</sub> = 39.4 MGOe) equivalent to that of N40M commercial-grade Nd-Fe-B, as well as superb thermal stability (coercivity coefficient |<em>β</em>| of 0.55%/K within the 293-413 K interval) and electrochemical resistance. These outstanding properties are closely correlated with three notable microstructural characteristics, including (1) an increasing fraction of the REFe<sub>2</sub> phase with raised Cu content, (2) the occurrence of a new-type Cu-dissolved REFe<sub>2</sub> phase with higher Nd/Pr and lower Ce content than conventional 1:2 phase, and (3) a Cu-dissolved RE-rich phase with deficient Fe. Above structural and chemical features are discussed on the basis of experimental studies, which allow for better continuity of non-ferromagnetic grain boundary phase and higher chemical stability of intergranular regions, thus enabling a good compatibility of magnetic and anti-corrosive performance. Our exploration of (Nd, Pr)H<sub>x</sub> and Cu synergy may pave a novel way for developing high-figure-of-merit Nd-Ce-Fe-B permanent magnets that rival the commercial Nd-Fe-B counterpart.</p>
materials science, multidisciplinary,metallurgy & metallurgical engineering