Evaluation of core-shell structure and grain boundary structure in multi-main-phase Nd-Y-Fe-B sintered magnet by grain boundary modification
Sining Fan,Mengxin Jin,Guangfei Ding,Xiaodong Fan,Shuai Guo,Bo Zheng,Renjie Chen,Aru Yan,Bin Meng
DOI: https://doi.org/10.1016/j.jallcom.2022.167673
IF: 6.2
2023-01-15
Journal of Alloys and Compounds
Abstract:The grain boundary modification by Pr64Fe12Al9Ga15 addition was performed in the B-lean Nd-Y-Fe-B multi-main-phase (MMP) magnets. The effects of the additive on the microstructure and magnetic properties were investigated. A pronounced coercivity enhancement was achieved from 4.96 kOe to 8.15 kOe with 2 wt% Pr64Fe12Al9Ga15 addition, while the coercivity tended to be invariable with further increasing of Pr64Fe12Al9Ga15 content to 4, 6, and 8 wt%. Detailed microstructure analysis revealed that the significant amounts of RE6Fe13(Ga, Al)1 intergranular phase were generated by introducing Pr64Fe12Al9Ga15 additive in the B-lean Nd-Y-Fe-B MMP magnets. The formation of RE6Fe13(Ga, Al)1 contributed to the optimization of the distribution of grain boundary (GB) phase, strengthening the intergrain magnetic isolation. However, the further increases of the additive content led to the agglomeration of RE6Fe13(Ga, Al)1 in the triple junction region, which caused a reduction in remanence. Meanwhile, excessive addition for additives revealed that the thicker GB layer was unessential to further increase in coercivity, the intergranular exchange coupling had already been decoupled in magnets with adequate addition. In addition, more Pr atoms were primarily substituting the Nd atoms, but Y atoms were not substituted by Pr in the shell region of matrix grains. It was deemed that the magnetic anisotropy of the grain shell was essentially unchanged even with the formation of Pr-rich shell. These results reported here enlighten the microstructure design of Nd-Y-Fe-B MMP magnets.
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering