Abstract:In the current work, the yttria stabilized zirconia (YSZ) thermal barrier coatings (TBCs) have been fabricated by atmospheric plasma spraying. The failure mechanism of the TBCs during burner rig test (BRT) has been investigated via finite element modeling (FEM) and in-situ acoustic emission (AE) technique systematically. During the BRT, the oxygen-propane flame was heated onto the surface of the coating samples with the dwell time 3 min, then the surface and the backside of the coating samples were cooled by the compressed air simultaneously for 3 min. This can be viewed as one thermal cycle. Then repeat the same heating and cooling process. The history and distribution of the temperature along the through-thickness direction of the coating samples has been obtained via FEM, and the residual stress at different stages has been also calculated. The FEM results have indicated that large tensile stress and compressive stress existed at the heating stage and cooling stage of each thermal cycle, respectively. The crack propagation tends to occur at the initial period of heating stage in the BRT process. The in-situ acquisition of the AE signals during the BRT has also been adopted. The crack propagation patterns have been obtained based on the analysis of AE signals. The filtering technique has been used to exclude the disturbance of the noise in the process of BRT in order to capture the actual and effective AE signals which represent the crack propagation and the deformation of the coating systems. Based on the characteristic waveform of effective AE signals, the Fast Fourier Transformation (FFT) and wavelet transformation has been adopted to analyze the key distribution range of the amplitude and frequency. The investigation results indicate that the acquired AE signals during BRT mainly include signals which came from the plastic deformation of the substrate and creep of each layers, propagation of the vertical crack and propagation of the interfacial cracks (horizontal crack). The detailed failure mechanisms of the TBCs during BRT have been clarified in the current work.

Determination of Mixed-Mode Interfacial Fracture Toughness for Thermal Barrier Coatings

Microstructural analysis of the thermal fatigue tested Be/CuCrZr joint with artificial defects between Ti/Cu interlayers

Measurements of elastic modulus and fracture toughness of an air plasma sprayed thermal barrier coating using micro-cantilever bending

Evaluation of the cracked lap shear test for mixed-mode fracture toughness estimation of adhesive joints

Simulation of Residual Stresses and Their Effects on Thermal Barrier Coating Systems Using Finite Element Method

Determination of Interface Fracture Toughness of Adhesive Joint Subjected to Mixed-Mode Loading Using Finite Element Method

Determination and Analysis of Crack Growth Resistance in Plasma-Sprayed Thermal Barrier Coatings

Shakedown Analysis and Experimental Study of Thermal Barrier Coatings

In-Situ Characterization on Fracture Toughness of Thermal Barrier Coatings Under Tension by J-Integral with Digital Image Correlation at High Temperatures

Interfacial peeling loads in the TBC with an air hole: Analytical solutions and viscoplasticity modelling

Prediction of critical rupture of plasma-sprayed yttria stabilized zirconia thermal barrier coatings under burner rig test via finite element simulation and in-situ acoustic emission technique

A Diffusion-Coupled Cohesive Element Model for Cracking Analysis of Thermal Barrier Coatings

Experimental Investigation on High-Temperature Fatigue and Fracture Properties at the Interface Between Thermal Barrier Coatings (tbcs) and Nickel Based Superalloy Substrate

Computational analysis of thin coating layer failure using a cohesive model and gradient plasticity

RESEARCH PROGRESS ON THE EXPERIMENTAL MEASUREMENT METHODS OF MECHANICAL PROPERTIES OF THERMAL BARRIER COATINGS

High Temperature Fracture Toughness and Residual Stress in Thermal Barrier Coatings Evaluated by an In-Situ Indentation Method

Cross-scale modeling and elasto-plastic mechanical properties of TBC with 3D hill-like interface

Numerical and Experimental Investigation of Residual Stress in Thermal Barrier Coatings During Aps Process

Discrete element modeling of effect of interfacial roughness and pre-crack on crack propagation in thermal barrier coatings

Thermomechanical and Thermal Gradient Mechanical Fatigue Lifetime of Thermal Barrier Coating Systems

Fracture Behavior of TBCs with Cooling Hole Structure under Cyclic Thermal Loadings