Abstract:In recent years, structural adhesives have rapidly become the preferred alternative to resistance spot welding in fabricating stronger, lighter aluminum connections. Connections inevitably undergo and must withstand complex quasi-static and/or dynamic loads during their service life. Therefore, understanding how loading conditions affect the mechanical behavior of adhesive joints is vital to their design and the advancement of structural safety. Quasi-static and dynamic tests are performed to analyze both the strength and failure modes of aluminum 6062 substrates bonded by an adhesive (Darbond EP-1506) for an array of loading directions. An Arcan test device, which enables application of mixed-mode loads ranging from pure peel (mode I) to pure shear (mode II) to the adhesive layer, is employed in quasi-static testing. A self-designed medium-speed test machine is utilized to perform dynamic testing. To avoid severe system oscillations exhibited in force measurements during dynamic testing, the Arcan test device is replaced by a set of integrated fixtures to improve stiffness and reduce fixture weight. To induce manifold mechanical responses in the adherend and adhesive materials, the specimens are subjected to a mixture of transverse and shear forces. Experimental results demonstrate that the fracture displacement increases with an increase in testing angle of the applied force, indicating that ductile fracture predominates brittle fracture and governs failure when shear loading is significant in mixed loading scenarios, especially for dynamic tests. Furthermore, dynamic strengthening is observed in samples subjected to peel loading, but is undiscovered in samples tested under mixed loading conditions, where interfacial failure is more likely to occur compared to cohesive failure. This observation reveals that the cohesive zone is reinforced by the strain rate effect, whereas the interface between the adhesive and adherend does not experience this phenomenon.

Determination of Interface Fracture Toughness of Adhesive Joint Subjected to Mixed-Mode Loading Using Finite Element Method

Evaluation of the cracked lap shear test for mixed-mode fracture toughness estimation of adhesive joints

Determination of fracture toughness of an adhesive in civil engineering and interfacial damage analysis of carbon fiber reinforced polymer–steel structure bonded joints

Nonlinear Fracture Analysis of Delamination Crack Jumps in Laminated Composites

On the Fracture Resistance of Adhesively Jointing Structures

Computational Fracture Mechanics Assessment of Adhesive Joints

Estimation of fracture behavior of CFRP/CFRP adhesively bonded joints under mixed-mode conditions using a cohesive zone model

Experimental and numerical investigation on test methods for mode II fracture of composite‐titanium adhesively bonded structures

Experimental Investigation of the Mechanical Behavior of Aluminum Adhesive Joints under Mixed-Mode Loading Conditions

Finite Element Analysis of Crack Propagation in Adhesive Joints with Notched Adherends

Fracture analysis on die attach adhesives for stacked packages based on in-situ testing and cohesive zone model.

Fracture energy and cohesive law analysis of adhesives using a recently developed SCB joint: The influence of joint geometry and mode mixity

Mode II fatigue characteristics of a composite bonded joint with microstructured adhesive bondline through tailored sacrificial cracks

Estimation of CZM Parameters for Investigating the Interface Fracture of Adhesively Bonded Joints Under Mode I, Mode II, and Mixed‐Mode (I/II) Loading

A four-point bending technique for characterizing the interface fracture toughness between soft thin films and stiff substrates

Assessing critical fracture energy in mode I for bonded composite joints: A numerical–experimental approach with uncertainty analysis

Investigation on the Stable and Stick-Slip Crack Propagation Behaviors in Double Cantilever Beam Test

Analytical solution for the interfacial stress and energy release rate at failure initiation of the three-point bending test (ISO 14679:1997)

Influence of Loading Rate on the Cohesive Traction for Soft, Rubber-like Adhesive Layers Loaded in Modes I and III

Fracture Analysis of Highly Flexible Adhesives: Cohesive Zone Modelling across a Wide Spectrum of Temperatures and Strain Rates

Mode II fracture of an MMA adhesive layer: Theory versus experiment