Abstract:Large-area N-doped aligned carbon nanotube (ACNT) arrays perpendicular to the quartz substrate were synthesized by the chemical vapor deposition method (CVD) without template. Xylene and Ethylenediamine were selected as carbon and nitrogen feedstock respectively. Ferrocene was taken as the catalyst. Scanning electron microscopy (SEM) characterizations showed that the highly aligned synthesized ACNT arrays were composed of fairly straight carbon nanotubes with good graphite structures and high purity as confirmed by high resolution transmission electron microscopy (HRTEM) characterizations. Moreover, HRTEM characterizations also revealed the in-situ growth of "fullerene-like" structure in the carbon nanotubes for the first time. Raman spectrum revealed abundant single-walled carbon nanotubes in the ACNT arrays. X-ray photoelectron spectrum characterizations showed that N atom was incorporated in the ACNT arrays successfully and its percentage increased with the increase of nitrogen source in the feedstock. When the mole ratio of the N atom to C atom was equal to 1:1, the incorporated N atoms in the ACNT arrays could reach as high as 2.51% in mole unit.

Template Synthesis of High-Density Carbon Nanotube Arrays

Template-confined growth and structural characterization of amorphous carbon nanotubes

The Fabrication And Characterization Of N-Doped Aligned Carbon Nanotube Arrays In Large Area

Field Emission Property of Highly Ordered Monodispersed Carbon Nanotube Arrays

Synthesis of Carbon Nanotube Array Using Corona Discharge Plasma-Enhanced Chemical Vapor Deposition

Facile Synthesis of High Density Carbon Nanotube Array by a Deposition-Growth-densification Process

Synthesis Of Large Quantity Single-Walled Carbon Nanotubes By Arc Discharge

Synthesis of high quality, closely packed vertically aligned carbon nanotube array and a quantitative study of the influence of packing density on the collective thermal conductivity

SYNTHESIS OF ALIGNED CARBON NANOTUBES ARRAY BY RADIO FREQUENCY PLASMA-ENHANCED HOT FILAMENT CHEMICAL VAPOR DEPOSITION

Template-based synthesis of carbon nanofibres and their field emission characteristics

Growth of Well-Aligned Carbon Nanotube Arrays on Silicon Substrates Using Porous Alumina Film As a Nanotemplate

Controlled growth of carbon nanotubes in diameter and shape using template-synthesis method

Field Emission from Dense, Sparse, and Patterned Arrays of Carbon Nanofibers

Growth Of High-Quality Single-Wall Carbon Nanotubes Without Amorphous Carbon Formation

Plasma Enhanced Chemical Vapour Deposited Carbon Nanotubes for Field Emission Applications

Synthesis of alumina nanotubes using carbon nanotubes as templates

Rapid Growth of Well-Aligned Carbon Nanotube Arrays

Carbon Nanotubes Synthesized by Simple Thermal Chemical Vapor Deposition and Their Electrical Properties

Fabrication of well-aligned carbon nanofiber array and its gaseous-phase adsorption behavior

Template-Directed Synthesis of Boron Nitride Nanotube Arrays by Microwave Plasma Chemical Reaction

Synthesis and Characterizations of Amorphous Carbon Nanotubes by Pyrolysis of Ferrocene Confined Within Aam Templates