Abstract:SiC nanowires are excellent high-temperature electromagnetic wave (EMW) absorbing materials. However, their polymer matrix composites are difficult to work at temperatures above 300°C, while their ceramic matrix composites must be prepared above 1000°C in an inert atmosphere. Thus, for addressing the abovementioned problems, SiC/low-melting-point glass composites were well designed and prepared at 580°C in an air atmosphere. Based on the X-ray diffraction results, SiC nanowires were not oxidized during air atmosphere sintering because of the low sintering temperature. Additionally, SiC nanowires were uniformly distributed in the glass matrix material. The composites exhibited good mechanical and EMW absorption properties. As the filling ratio of SiC nanowires increased from 5wt% to 20wt%, the Vickers hardness and flexural strength of the composite reached HV 564 and 213 MPa, which were improved by 27.7% and 72.8%, respectively, compared with the low-melting-point glass. Meanwhile, the dielectric loss and EMW absorption ability of SiC nanowires at 8.2–12.4 GHz were also gradually improved. The dielectric loss ability of low-melting-point glass was close to 0. However, when the filling ratio of SiC nanowires was 20wt%, the composite showed a minimum reflection loss (RL) of −20.2 dB and an effective absorption (RL ≤ −10 dB) bandwidth of 2.3 GHz at an absorber layer thickness of 2.3 mm. The synergistic effect of polarization loss and conductivity loss in SiC nanowires was responsible for this improvement.

Effect of temperature on dielectric properties of Si3N4/SiO2 composite and silica ceramic

Optimization of Microstructure to Improve Si3n4 Ceramics with Thermal Conductivity and Mechanical Properties: Effect of Si and Α-Si3n4 Powder Composition

Effect of Different Forms of Silica on Sintering, Microstructure and Properties of Borosilicate Glass/al2o3 Composites

Multiple dielectric behavior of Cf-SiCNFs/Si3N4 ceramic composite at high temperatures

Influence of silicon carbide nanowires on the properties of Bi-B-Si-Zn-Al glass based low temperature co-fired ceramics

Effect of Composite Sintering Additives Containing Non-Oxide on Mechanical, Thermal and Dielectric Properties of Silicon Nitride Ceramics Substrate

Influence of sintering temperature on giant dielectric property of CaCu3Ti4O12

Effect of Bi-B-Si-Zn-Al glass additive on the properties of low-temperature sintered silicon carbide ceramics

Effect of interfacial area and particle size on the microstructure and dielectric properties of BaTiO3-SiO2 nanocomposites

Low Temperature Sintering and Properties of Ca–Al–B–Si–O Glass/ceramic Composites with Various Ceramic Fillers

Thermal conductivity and dielectric property of hot-pressing sintered AlN–BN ceramic composites

Effect of Sintering Additive Content on Mechanical and Dielectric Properties of Porous Si3N4/BN Composite Ceramics

Electromagnetic wave absorption and mechanical properties of SiC nanowire/low-melting-point glass composites sintered at 580°C in air

Low Temperature Sintering and Dielectric Properties of Ca- Ba-Al-B-Si-O Glass/Al_2 O_3 Composites for LTCC Applications

Effects of SiC contents on the microstructure and mechanical properties of Al4SiC4–SiC ceramic composites

Effects of Various Fillers on Sintering, Microstructures and Properties of Ca-Ba-Al-B-Si-O Glass/ceramic Composites

Microstructure and dielectric properties of glass/Al 2 O 3 composites with various low softening point borosilicate glasses

Effect of silica addition on microstructure, sintering behavior, and dielectric properties of borosilicate glass/alumina composites for LTCC application

Molecular dynamics simulation of the temperature effect on ideal mechanical properties of SiC/BN interface for SiCf/SiC composites

Variable temperature electron paramagnetic resonance studies of the NiZn ferrite/SiO2 nanocomposite

Low Temperature Sintering and Performance of Aluminum Nitride/Borosilicate Glass