Preparation and Microwave Properties of Ni0.5Zn0.5Fe2O4 Nanocrystalline Powder Prepared by Polyacrylamide Gel Process

MA Rui-ting,SHAO Zhong-cai,ZHANG Chun-li,LI Hong,TIAN Yan-wen
DOI: https://doi.org/10.3321/j.issn:1009-606x.2007.03.035
2007-01-01
Abstract:Nanocrystalline Ni0.5Zn0.5Fe2O4 powder was prepared using polyacrylamide gel method with acrylamide as monomer and N,N'-methylenediacrylamide as lattice agent.The analysis methods of Fourier transform infrared spectrometer(FI-IR),X-ray diffraction(XRD),transmission electron microscopy(TEM) and wave-guide were used to characterize the gel and the products after calcining.The XRD study shows that the dried gel is amorphous,the spinel Ni0.5Zn0.5Fe2O4 forms at and above 400 ℃.The grain size and the M-O metal and oxygen characteristic absorption bonds are dependant on heat treatment temperature.When the calcining temperatures are 600 and 800 ℃,the grain sizes are 10 and 30 nm identified by TEM,respectively.The FT-IR spectra illustrate that the M-O characteristic absorption bonds shift from 590 to 613 cm-1 when the calcining temperature is shifted from 400 to 800 ℃.The nanocrystalline Ni0.5Zn0.5Fe2O4 has both dielectric loss and magnetic loss,while the complex permittivity and complex permeability of Ni0.5Zn0.5Fe2O4 increase with increasing the heat treatment temperature in the frequency range of measurement.
What problem does this paper attempt to address?