Abstract:Fine-grained metals have attracted much interest due to the possibility to obtain both high strength and high ductility.Studies of the deformation mechanisms in fine-grained metals are therefore important,and can also help fill a gap in knowledge between nano-grained metals and conventional coarse-grained metals,which is an area of both scientific and industrial interest.For such an investigation it is very important to use a starting material with a simple microstructure.For this purpose spark plasma sintering(SPS) has been used to prepare samples of fully dense,fine-grained Al with average grain sizes ranging from 0.8μm to 5.2μm,in a fully recrystallized condition,with equiaxed grains and a random texture.The microstructures and mechanical properties of these sintered finegrained Al samples have been studied using EBSD,TEM and compression testing.Based on these studies,relationships between the microstructure and mechanical properties have been established. The results show that the formation of deformation microstructure depends on grain size.During deformation,all grains in samples with an average grain size of 5.2μm show grain subdivision by dislocation boundary formation,though few grains in a sample with an average grain size of 0.8μm show dislocation boundary formation.The mechanical properties of fine-grained Al show a transition in behavior with decreasing average grain size.For samples with an average grain size of 1.3μm,stressstrain curves show yield drop phenomenon,attributed to source-limited hardening.For a sample with an average grain size of 0.8μm,the stress-strain curve shows only limited work-hardening after yielding,in agreement with the observation of the limited formation of dislocation boundaries inside grains during deformation.For a sample with average grain size of 5.2μm the average dislocation boundary misorientation angle increases more quickly than in deformed conventional coarse-grained Al deformed to the same strain,due to the effect of increased volume fraction of grain boundaries and oxide particles.The strength of the SPS-prepared Al samples is higher than found for samples with identical grain sizes prepared by thermo-mechanical deformation,due to the presence of oxide particles,and to source-limited hardening for samples with average grain sizes smaller than 1.3μm.

Investigation of Deformation Microstructures in Spark Plasma Sintered Nickel

Refining Micron-Sized Grains to Nanoscale in Ni-Co Based Superalloy by Quasistatical Compressive Deformation at High Temperature

Abnormal Grain Growth: A Potential Way to Construct Gradient Structure

Effect of Grain Size on Deformation and Fracture of Inconel718: an In-Situ SEM-EBSD-DIC Investigation

Quantification of Deformation Microstructure at Ultra-Low Tensile Strain in Pure Al Prepared by Spark Plasma Sintering

In-situ EBSD study of deformation behavior of nickel-based superalloys during uniaxial tensile tests

Grain Orientation Induced Softening in Electrodeposited Gradient Nanostructured Nickel during Cold Rolling Deformation

Grain size dependent microstructure and texture evolution during dynamic deformation of nanocrystalline face-centered cubic materials

Texture and Deformation Structure Evolution During Rolling of Individual Grains of Columnar Grain Nickel

Deformation And Annealing Textures Of Extruded And Cold Rolled Pure Ni Single Crystals Of Cube Orientation

Microstructures and Mechanical Properties of Sintered Fine-Grained Al

In-situ Study of Microstructural Evolution and Local Strain Distribution During Tensile Loading of Near-Micrometre Grain Size Aluminium

Deformation Strain Inhomogeneity in Columnar Grain Nickel

Influence of Grain Size in the Near-Micrometre Regime on the Deformation Microstructure in Aluminium

Structure and Strength of Aluminum with Sub-Micrometer/micrometer Grain Size Prepared by Spark Plasma Sintering

Bending deformation and indentation hardness of electrochemically deposited nanocrystalline nickel-iron alloys

The deformation mechanism of nanocrystalline nickel under high strain rate

Nanoscale Origins of the Size Effect in the Compression Response of Single Crystal Ni-Base Superalloy Micro-Pillars

γ′-size effect on the deformation microstructure and texture in a Ni-based superalloy using in-situ neutron diffraction

Evolution of Orientations and Deformation Structures Within Individual Grains in Cold Rolled Columnar Grained Nickel

Orientation-Dependent Characteristics for Residual Grains During Hot Deformation of Nickel-Based Alloy 925