Abstract:Ultrafine binderless WC-based cemented carbides with varied amounts of AlN nano-powder (0–16wt.%) were fabricated by spark plasma sintering at 1600°C under a pressure of 50MPa with the assistance of VC and TaC as WC grain growth inhibitors. The densification behavior, phase composition, microstructure and mechanical properties of the as-prepared samples were investigated. During sintering, rapid sample shrinkage started at about 1050°C and ended at about 1550°C. X-ray diffraction analysis revealed that an appropriate addition amount of AlN nano-powder would be of help to limit the formation of W2C phase and promote the formation of solid solution phase of (V,W)C2 during sintering. As the added fraction of AlN nano-powder increased, the relative density of the samples initially increased and then decreased, reaching its maximum of about 99.6% when 3–5wt.% AlN nano-powder was added. Scanning electron microscopy examination indicated that the average size of WC grains in the samples was about 0.7μm and with increasing added fraction of AlN nano-powder, the abnormal growth of WC grains was suppressed and their sizes were somewhat reduced. Both the sample hardness and flexural strength first increased and then decreased with increasing added fraction of AlN nano-powder, reaching the maximum hardness of about 2400 HV10 with 3wt.% AlN nano-powder and maximum flexural strength of about 1250MPa with 5wt.% AlN nano-powder, respectively. However, the fracture toughness slightly decreased from 7.5 to 6.3MPa·m1/2 with increasing added fraction of AlN nano-powder.

Surface adsorption phenomenon during the preparation process of nano WC and ultrafine cemented carbide

Preparation of Ultra-Fine WC-Co Cermet and Its Wear Behavior

Microstructural Characterization of Nanostructured WC-Co Cemented Carbides

Ultrafine WC-Ni cemented carbides fabricated by spark plasma sintering

Ultrafine/nano WC-Co Cemented Carbide: Overview of Preparation and Key Technologies

Investigation of the Machined Surface Integrity of WC-High-Entropy Alloy Cemented Carbide

Ultrafine Binderless WC-based Cemented Carbides with Varied Amounts of AlN Nano-Powder Fabricated by Spark Plasma Sintering

Dissolving Mechanism of the WC/W2Cp in NiCrBSi Alloy and Surface Modification for the WC/W2Cp by Carburizing

Mechanical properties and erosion resistance of ceria nano-particle-doped ultrafine WC-12Co composite prepared by spark plasma sintering

Preparation Technology of Ultra-Fine Tungsten Carbide Powders: an Overview

Phase Composition and Microstructure of Binderless Wc-Zrc Cemented Carbides Fabricated by Spark Plasma Sintering

Decarbonization and Its Improvement of Coarse-Grained Low Cobalt Cemented Carbide Sintered by Microwave Irradiation

Research on Microstructure and Properties of Ultrafine Grained WC-Ni3Al Cemented Carbide

Sintering behavior of WC-10Co-V(C, N) nanocrystalline gradient cemented carbide

Effect of Metal Elements on Microstructure and Mechanical Properties of Ultrafine Cemented Carbide Prepared by SPS

Microstructures and Properties of WC-10 wt.%CoCrFeNiAlx Composite Cemented Carbides

Effects of nanocomposite grain growth inhibitors and multi-walled carbon nanotubes on the microstructure and mechanical properties of ultrafine cemented carbides

Comparative Study on Microstructure and Mechanical Properties of Coarse-grained WC-based Cemented Carbides Sintered with Ultrafine WC or (W+C) as Additives

Microstructure and Fracture Toughness of a WC-Fe Cemented Carbide Layer Produced by a Diffusion-Controlled Reaction

Study on interfacial cobalt phase between diamond film and cemented carbide insert

Effects of micro/nano CeO2 on the microstructure and properties of WC-10Co cemented carbides