Abstract:The preparation and characteristics of silicon nanoarrays is now an attractive areas of research. At present,most research focused on the optical and electrical properties and applications,and less field emission characteristics,as a mature technology of silicon planar support, silicon field emission cathode materials are easily compatible with the microelectronic integrated circuits, and so they have a broad application prospects.We present the fabrication of large-scale two dimensional periodic silicon nanoarrays using nanosphere lithography,and the field emission characteristics have been studied. The fabrication process includes following steps: first the crystalline silicon substrate was coated with a monolayer of self polystyrene (PS) spheres of 220 nm in diameter, then the sample was etched by reactive ion etching to produce silicon nanoarrays. AFM images of the nanoarrays show that the tips stand 60～70 nm high and the area density can achieve 6×109/cm2. All field emission measurements were performed at a vacuum of 1.0×10-4 Pa or better. Expected to improve the field emission characteristics, about 60 nm thickness of a amorphous carbon film was deposited on top of the silicon nanoarrays by plasma-enhanced chemical vapour deposition. Field emission results show that compared to silicon nanoarrays, silicon nanoarrays coated with a thin a-C film effectively lower the threshold fields, approximately 8.1 V/μm, while field enhancement factor increased. When the electric field intensity reached 20 V/μm, the current density can reach about 1.4 mA/cm2. The improvement of field emission originates from the anisotropic structure of the films,when conductive sp2 clusters embedded in an insulating sp3 matrix,the electric field has been enhanced.

Self-assembled Au–Si Alloy Nanocones: Synthesis and Electron Field Emission Characteristics

Formation and Field Emission Characteristics of Amorphous and Crystalline Si Nanoarrays

Enhanced Field Emission of Au Nanoparticle-Decorated SiC Nanowires

Synthesis and Field Emission Property of SiCN Cone Arrays

Synthesis and field emission properties of aluminum nitride nanocones

FORMATION AND FIELD EMISSION CHARACTERISTICS OF AMORPHOUS AND CRYSTALLINE <font>Si</font> NANOARRAYS

Si Nanowire With Integrated Space-Charge- Limited Conducted Schottky Junction for Enhancing Field Electron Emission and Its Gated Devices

Synthesis of Large-Area Germanium Cone-Arrays for Application in Electron Field Emission

Nanoparticle-density-dependent Field Emission of Surface-Decorated SiC Nanowires

Low Reflectance Gaas Nano-Cones Fabricated By Colloidal Lithography For Solar Cells

Electron Field Emission Characteristics from Single-crystal Silicon Nanoarrays Fabricated by Direct Lithography with Nanosphere Mask

Laser microstructuring of Si surfaces for low-threshold field-electron emission

P1&#x2013;17: Controlled Synthesis of Au and Ag/Au Nanoparticles for Fabrication of N-Doped Amorphous Si Nanowire Field Emission Cathode

Silicon Nano-Wires Fabricated by Thermal Evaporation of Silicon Wafer

Field emission of uniform carbon cone arrays grown on porous silicon substrate

Fabrication of cone-shaped CNF/SiC-coated Si-nanocone composite structures and their excellent field emission performance

Well-aligned SiC nanoneedle arrays for excellent field emitters

Enhanced Electron Field Emission from Dense Si Nano-Dots Prepared by Laser Crystallization of Ultrathin Amorphous Si Films

Self-Assembled Growth and Optical Emission of Silver-Capped Silicon Nanowires

Enhanced Field Emission Properties from Well-Aligned ZnO Nanocones

Superior integrated field emission cathode with ultralow turn‐on field and high stability based on SiC nanocone arrays