Characteristics of High Ductility and Low Shrinkage Engineered Cementitious Composite and Its Applications

张君,公成旭,居贤春

DOI: https://doi.org/10.13243/j.cnki.slxb.2011.12.009

2011-01-01

Abstract:Micro-mechanically designed engineered cementitious composite （ECC） is one of the successful materials for ductility improvement of the cement based materials. This paper reports the mechanical properties of a new class of engineered cementitious composite recently developed with characteristic of low drying shrinkage. Experimental results show that drying shrinkage of the composite is greatly reduced as using the low shrinkage cementitious material in matrix, while the composite remains strain-hardening and multiple cracking characteristics. The measured drying shrinkage strain in 28 days is only 0.12 to 0.20 of shrinkage of the traditional ECC. The average tensile strain capacity after 28 days curing can achieve 2.5% of the low shrinkage ECC with tensile strength of 4-5MPa. The experimental results also show that the composite with compressive strength ranging from 20 to 60MPa can be obtained by varying w/c from 0.55 to 0.25, while remaining the tensile strain hardening and multiple cracking performances. A significant plasticity, like yielding of metal, is found under compressive load after peak stress. Finally, recent application studies are introduced.