High-temperature phase transition and magnetic property of LaFe11.6Si1.4 compound
Xiang Chen,Yungui Chen,Yongbai Tang
DOI: https://doi.org/10.1016/j.jallcom.2011.05.054
IF: 6.2
2011-01-01
Journal of Alloys and Compounds
Abstract:The LaFe 11.6 Si 1.4 compounds are prepared by arc-melting and then annealed at different high temperatures from 1323 K(5 h) to 1623 K(2 h). The powder X-ray diffraction and metallographic microscopy show that 1423 K and 1523 K are two curial temperatures, at which large amount of 1:13 phase begins to form and the most amount of 1:13 phase is obtained, respectively. With annealing temperature increasing to 1573 K and 1623 K, a new phase of La 5 Si 3 is detected in LaFe 11.6 Si 1.4 compound. According to the DSC curve of as-cast LaFe 11.6 Si 1.4 compound and the X-ray patterns of annealed LaFe 11.6 Si 1.4 compounds, the high-temperature phase transition process is analyzed. For studying the influence of different high-temperature and short-time annealing on magnetic property, the Curie temperature, thermal and magnetic hysteresis, magnetocaloric effect of LaFe 11.6 Si 1.4 compound annealed at different temperatures are also investigated. Keywords LaFe11.6Si1.4 compound High-temperature and short-time annealing Phase transition Magnetic property 1 Introduction LaFe 13− x Si x compounds with 1.1 ≤ x ≤ 1.6 are enjoying interest in the magnetic materials community due to the observation of a large MCE in LaFe 11.4 Si 1.6 compound [1] . Those compounds undergo a first-order magnetic transition at T C about 200 K, and an itinerant-electron metamagnetic (IEM) transition just above T C [2,3] , which result in a large magnetocaloric effect (MCE). Because of the low price of starting materials and excluding deleterious elements, LaFe 13− x Si x compounds are the hot research points in magnetic refrigerant materials field for long time [4–9] . Recently, the main studies about LaFe 13− x Si x compounds focused on how to enhance T C , improve magnetocaloric properties, reduce the large thermal and magnetic hysteresis, and improve the corrosion resistant property. Researches found that the T C can adjust according to the hydrogen content in LaFe 13− x Si x hydrides while the large magnetic entropy change is retained, and both thermal and magnetic hysteresis are remarkably reduced because of the weakness of the itinerant-electron metamagnetic transition after hydrogenation [10–12] . The doping of B as interstitial can help to form 1:13 phase in as-cast LaFe 13− x Si x B y compounds accompanied Fe 2 B phase appearance [13] , and the thermal and magnetic hysteresis of LaFe 13− x Si x B y compounds is less than that of mother alloy [14–16] . But the Fe 2 B phase cannot be eliminated after the as-cast LaFe 13− x Si x B y compounds being annealed and the magnetocaloric effect decrease. The corrosion behavior and inhibition corrosion of La(Fe 0.94 Co 0.06 ) 11.7 Si 1.3 compound and LaFe 11.6 Si 1.4 in different solutions have been investigated [17–19] . The result shows that these alkaline solutions is necessary to ensure that a protection film can be formed on the surface of metal and have a good inhibition effect on the LaFe 13− x Si x compounds in a certain. Although the La(Fe 1− x Co x ) 11.9 Si 1.1 compounds with 0.055 < x < 0.122 produced by powder metallurgy, La(Fe0 .745 Co 0.17 Si 0.085 ) 13 ribbons prepared by melt spinning and annealed for a shorter time, and the LaFe 13– x Si x ( x = 1.4, 1.6, 1.8, 2.0) series synthesized by high energy ball-milling have been investigated [20–22] , most of LaFe 13− x Si x compounds with NaZn13-type structure (hereinafter 1:13 phase) are prepared by long time annealing for several weeks at between 1173 K and 1373 K, and then quenching rapidly in medium. In the LaFe 13− x Si x compounds, 1:13 phase is hard to be obtained directly from common solidification process due to the intrinsic incompleteness of a peritectic reaction: γ-Fe + L → La(Fe,Si)13( τ 1a ), which often results in the mixed microstructure of α-Fe + La(Fe,Si)13( τ 1a ) + LaFeSi( τ 4 ) [23] . For shorting the annealing time, some researchers used melt-spun or rapid quenching/short-time annealing at about 1273 K to prepare 1:13 phase [24–26] . Compared with the arc-melting/long time annealing, the annealing time reduces to a few minutes or a few hours, but the preparation process is more complex, and most of annealed LaFe 13− x Si x compounds contained a small amount of α-Fe phase. Recently, our group used the arc-melting/high-temperature and short-time annealing to prepare 1:13 phase, the result showed the samples also contained a small amount of α-Fe phase [27] . For further improving the preparation process of La(Fe, Si) 13 compounds, the study of high-temperature phase transition of as-cast La(Fe, Si) 13 compounds is necessary. Up to now, no elaborate study of the phase transition is made when the as-cast La(Fe,Si) 13 compounds are annealed. In this paper, the influence of different short-time and high-temperature annealing of as-cast LaFe 11.6 Si 1.4 compound from 1323 K to 1623 K on phase relation is investigated. According to the DSC curve of as-cast compound and the X-ray patterns of annealed compounds, the high-temperature phase transition process is analyzed. In addition, the phase relation, microstructure, thermal and magnetic hysteresis, and magnetocaloric effects of LaFe 11.6 Si 1.4 compounds prepared by the two stages annealing are also studied. 2 Experimental details Approximately 10 g polycrystalline LaFe 11.6 Si 1.4 buttons were fabricated by conventional arc melting in a high purity argon atmosphere using high purity (La: 99.4 wt%, Fe: 99.9 wt%, and Si: 99.9999 wt%) elements, the compounds were re-melted five times to achieve a homogeneous composition. The as-cast compounds were annealed as followed process: 1323 K for 5 h (hereinafter h), 1373 K(5 h),1423 K, 1453 K(5 h), 1473 K(5 h), 1503 K(5 h), 1523 K(5 h), 1373 K(2 h) + 1523 K(5 h), 1523 K(5 h) + 1373 K(2 h), 1543 K(5 h), 1573 K(4 h), 1623 K(2 h), 1523 K(5 h) + 1623 K(2 h), and 1373 K(2 h) + 1523 K(5 h), and 1523 K(7 h) + 1373 K(2 h), respectively, in a molybdenum wire furnace of 3 × 10 −3 Pa vacuum, and then by furnace cooling down to room temperature. The phase purity and crystal structures observation were determined by powder x-ray diffraction (XRD) using Cu ( K α ) radiation. Scanning electron microscope (SEM) and energy disperse spectroscopy (EDS) observation are carried by Hitachi-S-3400 N. The phase transition of the compound was studied by Differential Scanning Calorimetry (DSC) in Ar gas atmosphere from 300 to 1773 K at 10 K/min. Magnetic measurements were performed using a vibrating-sample magnetometer (VSM, Lakeshore 7410). The Curie temperature ( T C ) were determined from the maxima of dM / dT of the M – T curves, which were measured in an applied magnetic field of H = 0.02 T. The magnetic entropy changes Δ S M ( T , H ) were calculated from isothermal magnetization curves ( M – H curves) under a magnetic fields of 0–2 T in the vicinity of the Curie temperature using the thermodynamic Maxwell relation [28] . 3 Result and discussion 3.1 The phase relation and microstructure of the single stage high-temperature and short-time annealing The long time annealing at about 1323 K is often used to prepare the LaFe 13− x Si x compounds with 1:13 phase, detailed studies of the heat treatment of LaFe 13− x Si x compounds are reported in few articles. For studying the effect of different higher-temperature and short-time heat treatment on the phase relation of LaFe 11.6 Si 1.4 compounds, different annealing temperatures were experimented. Fig. 1 shows the XRD patterns of LaFe 11.6 Si 1.4 compounds annealed at different high temperatures from 1323 K to 1623 K, and the as-cast compound respectively. One can find that the as-cast LaFe 11.6 Si 1.4 compound mainly consists of α-Fe and LaFeSi phases. In addition, the appearance of three minor peaks at 2 θ = 35, 38.5, and 46.8 indicates that there is a small amount of the third phase crystallized as 1:13 phase. It is well known that the temperature of annealing is higher, and the speed of diffusion of atoms is just larger during the high-temperature and solid-phase diffusion reaction. Thus, with increasing of annealing temperature from 1323 K to 1423 K, the amount of 1:13 phase gradually increases and α-Fe and LaFeSi phases gradually reduce. But compared the XRD patterns, one can find that the amount of 1:13 phase in the compound annealed at 1423 K is obviously more than that of other compounds annealed at lower temperatures. It indicates that 1423 K is a critical temperature to form 1:13 phase. The speed of phase transforming to form 1:13 phase is very slow when the annealing temperatures are lower than 1423 K. With the temperature increasing from 1423 K to 1523 K, α-Fe and LaFeSi phases in the LaFe 11.6 Si 1.4 compounds reduce in turn. The LaFeSi phase is rarely observed in the XRD pattern when the annealing temperatures reach 1503 K and 1523 K. Although the α-Fe always exists in the LaFe 11.6 Si 1.4 compounds, the amount of α-Fe is very small in the compounds annealed at 1503 K and 1523 K, especially at 1523 K. Thus, 1523 K is also a critical temperature for obtaining the 1:13 phase during the high-temperature and short-time annealing of as-cast LaFe 11.6 Si 1.4 compound. Our result that there is a small amount of α-Fe besides 1:13 main phase in the XRD patterns is accordant to some references, which reported that the La(Fe,Si) 13 compounds prepared by annealing for long time and then quenching rapidly in medium or furnace cooling to room temperature also contained the 1:13 main phase and small amount of α-Fe [29–32] . This indicates that high-temperature and short-time annealing at 1523 K is an effective and feasible method to prepare LaFe 11.6 Si 1.4 compounds with 1:13 phase. To further observe the effect of annealing temperature on the phase relation, the as-cast LaFe 11.6 Si 1.4 compounds are annealed at 1543 K(5 h), 1573 K(4 h), 1623 K(2 h), and 1523 K(5 h) + 1623 K(2 h), respectively. When the annealing temperature increases to 1573 K and 1623 K, there is a new phase crystallized as La 5 Si 3 phase whose the strongest diffraction peak is at 2 θ = 31.5, and more La 5 Si 3 phase appears with higher annealing temperature. The LaFe 11.6 Si 1.4 compound annealed at 1523 K(5 h) + 1623 K(2 h) also contains a certain amount of La 5 Si 3 phase, which is not observed in the XRD pattern of LaFe 11.6 Si 1.4 compound annealed at 1523 K(5 h). The amount of α-Fe in the LaFe 11.6 Si 1.4 compounds annealed at 1573 K(4 h), 1623 K(2 h), and 1523 K(5 h) + 1623 K(2 h) is obviously more than that in the compound annealed at 1523 K(5 h). In addition, there is no diffraction peaks of La 5 Si 3 phase in the compound annealed at 1543 K(5 h), but the amount of α-Fe is more than that of LaFe 11.6 Si 1.4 compound annealed at 1523 K(5 h). In all, the most amount of 1:13 phase is obtained when the as cast LaFe 11.6 Si 1.4 compounds is annealed at 1523 K among the above single stage annealing under the same time. Fig. 2 demonstrates the backscattered SEM micrographs of the annealed LaFe 11.6 Si 1.4 compounds and as-cast compound. The different phases in these compounds can be identified by XRD and EDS analysis. The phase relation and the amount of different phases are in agreement with the XRD patterns, as shown in Figs. 1 and 2 . Through the refine analysis, we find the 1:13 phase locates between α-Fe and LaFeSi phase, but the amount is so small that it hard to be observed in the SEM micrographs of the annealed LaFe 11.6 Si 1.4 at 1373 K(5 h) and as-cast compounds, as shown in Fig. 2 (a) and (b). The SEM micrographs also shows that 1423 K and 1523 K are two critical temperatures during the high-temperature and short-time annealing of as-cast LaFe 11.6 Si 1.4 compounds, at which large amount of 1:13 phase begins to form and the most amount of 1:13 phase is obtained, respectively. 3.2 The analysis of high-temperature phase transition of as-cast LaFe 11.6 Si 1.4 compound In order to study high-temperature phase transition during the annealing process, DSC measurement was performed. Fig. 3 shows the DSC curve of massive as-cast LaFe 11.6 Si 1.4 compound during the heating process. There are four main endothermal peaks; the temperature of peaks is 1407.6 K, 1530.5 K, 1593.1 K, and 1739.3 K, respectively. In as-cast LaFe 11.6 Si 1.4 compound, α-Fe is primary phase, La(Fe,Si) 13 is peritectic phase, and LaFeSi is solidifying phase of residual liquid, respectively. It is universally acknowledged that the 1:13 phase should be formed through γ-Fe and LaFeSi phase if the annealing temperature is higher than 1185 K, which is the temperature of structural transition between α-Fe and γ-Fe. Based on the analysis of EDS, we find that α-Fe in as-cast LaFe 11.6 Si 1.4 compound is Fe(Si) solid solution, the atomic percent of Fe and Si is 94.85 at% and 5.15 at%, respectively. In the Fe–Si binary phase diagram, there exists the phase transition between γ-Fe and α-Fe only when the Si at% is less than 3.8 at% in Fe(Si) solid solution [33] . Thus, there is only α-Fe during the annealing process of as-cast LaFe 11.6 Si 1.4 compound, and the 1:13 phase is formed through α-Fe + LaFeSi → La(Fe,Si) 13 . According to the phase rule, the melting point of α-Fe is the highest, that of LaFeSi phase is the lowest in as-cast LaFe 11.6 Si 1.4 compound, and that of peritectic phase is between the melting point of primary phase (α-Fe) and the temperature of peritectic reaction. Combining with the Fe–Si binary phase diagram, one can easily come to the conclusion that 1739.3 K in the DSC curve is the melting point of Fe(Si) solid solution. Based on the result that large amount of 1:13 phase begins to form and the most amount of 1:13 phase is obtained when the as-cast LaFe 11.6 Si 1.4 compound is annealed at 1423 K and 1523 K, respectively, 1407.6 K and 1530.5 K are the melting point of LaFeSi phase and the temperature of peritectic reaction: α-Fe + L → La(Fe,Si) 13 , respectively. In addition, 1593.1 K is the melting point of 1:13 phase. Thus, when the annealing temperature is near 1593.1 K, the non-equilibrium freezing of liquid 1:13 phase leads to the appearance of La 5 Si 3 phase. The tradition method of preparing LaFe 11.6 Si 1.4 compound is by long-time annealing at about between 1173 K and 1373 K, and the annealing temperature is lower than melting point of LaFeSi phase (about the 1407.6 K). Under this situation, the 1:13 phase is formed through a peritectoid reaction between the α-Fe and the solid LaFeSi phases; it needs long time to complete solid state diffusion reaction. But when the annealing temperature is near the point of peritectic reaction, the 1:13 phase is formed through a peritectic reaction between the α-Fe and liquid phase, which is faster than the peritectoid reaction between α-Fe and solid state LaFeSi phase. Thus, there is the most amount of 1:13 phase in the LaFe 11.6 Si 1.4 compound annealed at 1523 K under the same annealing time. 3.3 The two stages high-temperature and short-time annealing Combining the result that most amount of 1:13 phase is obtained when the as cast LaFe 11.6 Si 1.4 compound is annealed at 1523 K in high-temperature and short-time annealing process with the traditional preparation method that the as-cast La(Fe,Si) 13 compound is annealed at about 1373 K for long time. Two stages annealing are carried, they are 1373 K(2 h) + 1523 K(5 h), and 1523 K(7 h) + 1373 K(2 h), respectively. The aims of annealing of low temperature (1373 K) and high temperature (1523 K) are increasing the chemic driving force and diffused driving force of phase transition, respectively. Figs. 4 and 5 are the XRD patterns and SEM micrographs of the LaFe 11.6 Si 1.4 compounds annealed at 1523 K(5 h) and different two stages. Three compounds consist of the main 1:13 phase and a certain amount impurities. Although it is hard to be observed from XRD patterns, very small amount of LaFeSi phase (white phase) can be observed in SEM micrographs. In the SEM micrographs, the black phase (α-Fe) and white phase (LaFeSi) in LaFe 11.6 Si 1.4 compound annealed at 1523K(7 h) + 1373K(2 h) are obviously less than that of others, which attributes to the annealing time at 1523 K is longer than others. In traditional preparation method, the single 1:13 phase compounds are almost prepared through long time annealing and then quenched in ice water or liquid nitrogen, and slow cooling is believed to induce the lower-temperature phases, such as 1:1:1 phase. But in our work, LaFeSi phase in the compounds annealed at 1523 K(7 h) + 1373 K(2 h) is not more than that in the compound annealed at 1523 K(5 h). Thus, the LaFeSi phase also can come from the incompleteness of peritectoid reaction, and not the slow cooling process. Up to now, there has no report to discuss whether the α-Fe and LaFeSi phases come from the incompleteness of peritectoid reaction or the slow cooling process. 3.4 Magnetic property Fig. 6 (a–c) displays the temperature dependent magnetization measured under 0.02 T in heating and cooling processes for LaFe 11.6 Si 1.4 compounds annealed at 1523 K(5 h), 1373 K(2 h) + 1523 K(5 h), and 1523 K(7 h) + 1373 K(2 h), respectively. T C is defined as the maximum of dM / dT in heating process. The difference of above three compounds’ T C is little, they are about 190 K. Temperature hysteresis is an important index for magnetic refrigeration material, and it is defined as the difference between T C (heating process) and T C (cooling process). To some extent, the value of temperature hysteresis is response to the first-order magnetic transition intensity. From Fig. 6 (a–c), one can find that three compounds have the temperature hysteresis phenomenon, and the value is about 2 K. The isothermal magnetization curves measured at different temperature in the vicinity of T C are shown in Fig. 7 (a–c) for three LaFe 11.6 Si 1.4 compounds. The measurements were performed in field increasing process. In order to check whether the isothermal magnetization process involves magnetic hysteresis, one of M – H curves was measured during field up and down at near T C . There is a field-induced itinerant-electron metamagnetic (IEM) transition from the paramagnetic state to the ferromagnetic state in the range of 2 K above T C . It indicates that the initiated critical field ( H C ) of field-induced IEM transition is lower than 2 T. Magnetic hysteresis is also response to the first-order magnetic transition intensity, which is defined as the enclosed area between the ascending and descending branches of magnetization curve. The magnetic hysteresis loss of compounds annealed at 1523 K(5 h) and 1373 K(2 h) + 1523 K(5 h) is smaller than that of compound annealed at 1523 K(7 h) + 1373 K(2 h), their value are 36.5, 39.7, and 46.8 J/kg, at 189, 190, and 191 K, respectively. Fig. 8 shows the compared Arrott plots of the samples. One can find that negative slopes appear in all samples, and the value of slope increases in sequential order. According to the I – S model, negative slope in Arrott plots curve often indicates a first order transition and the linear relation in Arrott plot above T C implies that a second-order magnetic transition occurs. Thus, all samples have the first order of magnetic transition behavior, and the first-order of magnetic transition behavior becomes intensity in sequential order. Because the first-order magnetic refrigerant materials have magnetoelastic coupling or magnetovolume coupling characteristic, there still exists the issue about whether the Maxwell equations suits to calculate the magnetic entropy change of those materials. Sun et al. pointed out that the Maxwell relation and the Clausius–Clapeyron equation can give similar magnetic entropy change for an idealized first-order transition [5,34] . But in reality, a first-order phase transition occurs in a finite temperature range, and two phases may coexist in the transition process. In this case, the Maxwell relation could yield a spurious Δ S peak in the vicinity of the Curie temperature T C . Considering the fact that magnetic field affects only the magnetic state of PM phase, which coexists with the FM phase near T C , only the PM phase contributes to the thermal effect. Liu et al. established a modified equation for calculating Δ S in reference [31] : Δ S [( T 1 + T 2 )/2] = ∑ 1 /( T 1 − T 2 ). Fig. 9 shows the Δ S M ( T , H ) calculated by using Maxwell relation based on the magnetization data as functions of temperature and magnetic field for LaFe 11.6 Si 1.4 annealed by different processes. Because the experimental field is higher than the H C of field-induced IEM transition, Δ S M ( T , H ) peaks have asymmetrical broad phenomenon to higher temperature above T C . The value of maximum Δ S M ( T , H ) is 18.5, 21.5, and 25.3 J/kg K for three compounds near T C , the change trend of maximum Δ S M ( T , H ) is same to the first-order behavior of the magnetic transition in compounds. But from the M – H curves, as shown in Fig. 7 , one can find that the compound LaFe 11.6 Si 1.4 present a mixed magnetic phase in the temperature range near T C , especially in the samples annealed at 1523 K(5 h) and 1523 K(7 h) + 1373 K(2 h). Thus, the use of the Maxwell relation for the evaluation of the entropy change close to the magnetic transition is not valid. More realistic values of the entropy change can be obtained based on the approaches developed in Ref. [35] . The result showed realistic values of the entropy change near T C obtained as in Ref. [35] is 11.3 and 17.8 J/kg K for 1523 K(5 h) and 1523 K(7 h) + 1373 K(2 h), respectively, they are smaller than those obtained by using the Maxwell relation. In addition, according to the Fe–Si binary phase diagram, the Curie temperature of α-Fe(Si) is far higher than room temperature, α-Fe(Si) is at ferromagnetic state and has no the magnetic transition between ferromagnetic and paramagnetic. Thus, the magnetic entropy change of α-Fe(Si) is very small during magnetization and demagnetization process, and it is negligible in the calculation of the magnetic entropy change Δ S in this work. 4 Conclusions Combining the DSC of as-cast massive LaFe 11.6 Si 1.4 compound with the X-ray patterns of LaFe 11.6 Si 1.4 compounds annealed at different high temperatures from 1323 K(5 h) to 1623 K(2 h), the high temperature phase transition process is analyzed. Large amount of 1:13 phase begins to form in LaFe 11.6 Si 1.4 compounds when the annealing temperature is higher than the melting point of LaFeSi phase (about the 1407 K). Because 1523 K is close to the temperature of peritectic reaction: α-Fe + L → La(Fe, Si)13, thus the most amount of 1:13 phase is obtained in the LaFe 11.6 Si 1.4 compounds annealed at 1523 K under the same annealing time. The non-equilibrium freezing of liquid 1:13 phase leads to the appearance of La 5 Si 3 phase when the annealing temperature is near the melting point of 1:13 phase. The phase relation and microstructure of the LaFe 11.6 Si 1.4 compounds annealed at 1523 K(5 h), 1373 K(2 h) + 1523 K(5 h) and 1523 K(7 h) + 1373 K(2 h), show that longer annealing time is helpful to decrease the impurity phases, especially at 1523 K. The magnetic measurement shows that above three compounds keep the first-order of magnetic transition behavior at T C (about 190 K). The values of the maximal magnetic entropy change Δ S M ( T , H ) of the samples obtained by Maxwell relation are 18.5, 21.5, and 25.3 J ˜ kg K , respectively under the field of 0–2 T. Acknowledgments The present work was supported by the Key Project of National Natural Science Foundation of China (grant number 50731007 ) and the National High Technology Research and Development Program of China (grant number 2007AA03Z440 ). References [1] F.X. Hu B.G. Shen J.R. Sun Z.H. Cheng G.H. Rao X.X. Zhang Appl Phys Lett. 78 2001 3675 [2] K. Fukamichi A. Fujita S. Fujieda J. Alloys Compd. 408 2006 307 [3] A. Fujita K. Fukamichi J. Alloys Compd. 404 2005 554 [4] A. Fujita S. Koiwai S. Fujieda K. Fukamichi T. Kobayashi H. Tsuji J. Appl. Phys. 105 2009 07A936 [5] B.G. Shen J.R. Sun F.X. Hu H.W. Zhang Z.H. Cheng Adv. Mater. 21 2009 4545 [6] H. Zhang Y. Long Q. Cao M. Zou K.A. Gschneidner Jr. V.K. Pecharsky J. Alloys Compd. 509 2011 3746 [7] A. Fujita S. Fujieda K. Fukamichi J. Phys. D: Appl. Phys. 44 2011 064013 [8] K. Morrison J. Lyubina J.D. Moore A.D. Caplin1 K.G. Sandeman O. Gutfleisch L.F. Cohen J. Phys. D: Appl. Phys. 43 2010 132001 [9] S.J. Kim K.J. Lee M.H. Jung H.J. Oh Y.S. Kwon J. Magn. Magn. Mater. 323 2011 1094 [10] M. Rosca M. Balli D. Fruchart D. Gignoux E.K. Hlil S. Miraglia B. Ouladdiaf P. Wolfers J. Alloys Compd. 490 2010 50 [11] C. Wang Y. Long T. Ma B. Fu R. Ye Y. Chang F. Hu J. Shen J. Appl. Phys. 109 2011 07A910 [12] J.-l. Zhao J. Shen F.-x. Hu Y.-x. Li J.-r. Sun B.-g. Shen J. Appl. Phys. 107 2010 113911 [13] H. Zhang Y. Long Q. Cao Ya. Mudryk M. Zou K.A. Gschneidner Jr. V.K. Pecharsky J. Magn. Magn. Mater. 322 2010 1710 [14] S. Jun W. Fang J.-L. Zhao J.-F. Wu M.-Q. Gong F.-X. Hu Y.-X. Li J.-R. Sun B.-G. Shen J. Appl. Phys. 107 2010 09A909 [15] Z. Lin S. Li M. Liu S.-Y. Tsai J.-G. Duh M. Liu F. Xu J. Magn. Magn. Mater. 323 2011 1741 [16] X. Chen Y. Chen Y. Tang J. Alloys Compd. 509 2011 2864 [17] M. Zhang Y. Long R.-c. Ye Y.-q. Chang J. Alloys Compd. 509 2011 3627 [18] E.Y. Zhang Y.G. Chenand Y.B. Tang Mater. Chem. Phys. 127 2011 1 [19] M. Zhang R. Ye Y. Long Y. Chang J. Rare Earth 29 2011 138 [20] B.R. Hansen L. Theil Kuhn C.R.H. Bahl M. Lundberg C. Ancona-Torres M. Katter J. Magn. Magn. Mater. 322 2010 3447 [21] M. Jasinski J. Liu S. Jacobs C. Zimm J. Appl. Phys. 107 2010 09A953 [22] V. Paul-Boncour L. Bessais Intermetallics 18 2010 2301 [23] V. Raghavan J. Phase Equilib. 22 2001 158 [24] A. Yan K.-H. Müller O. Gutfleisch J. Appl. Phys. 97 2005 036102 [25] X.B. Liu Z. Altounian GHTu J. Phys.: Condens. Matter 16 2004 8043 [26] Y. Zhu K. Xie X. Song Z. Sun W. Lv J. Alloys Compd. 392 2005 20 [27] T. Liu Y. Chen Y. Tang S. Xiao E. Zhang J.w. Wang J. Alloys Compd. 475 2008 672 [28] M. Foldeaki R. Chahine T.K. Bose J. Appl. Phys. 77 1995 3528 [29] F.X. Hu M. Ilyn A.M. Tishin J. Appl. Phys. 93 2003 5503 [30] F.X. Hu X.L. Qian J.R. Sun G.J. Wang X.X. Zhang Z.H. Cheng etal J. Appl. Phys. 92 2002 3620 [31] S.H. Xie J.Q. Li Y.H. Zhuang J. Magn. Magn. Mater. 311 2007 589 [32] G.F. Wang L. Song F.A. Li Z.Q. Ou O. Tegus E. BrÜck K.H.J. Buschow J. Magn. Magn. Mater. 321 2009 3548 [33] F.A. Shunk Constitution of Binary Alloys second supplement 1969 Mcgraw-Hill Book Co New York [34] J.R. Sun F.X. Hu B.G. Shen Phys. Rev. Lett. 85 2000 4191 [35] G.J. Liu J.R. Sun J. Shen B. Gao H.W. Zhang F.X. Hu B.G. Shen Appl. Phys. Lett. 90 2007 032507