Abstract:A preparation method of anti-oxidation superfine copper powder belongs to the powder technical field. The process flow of the method is as follows: taking soluble divalent cupric salt as a starting material for making cupric salt solution, adding and evenly mixing a dispersant and a trace additive, then adding NaOH solution to the cupric salt solution with the NaOH/Cu mol ratio being 2 to cause the Cu to precipitate as Cu(OH)2, adding a hydrazine hydrate as a reducing agent to obtained jelly with the N2H4/Cu mol ratio being 1.5-2.5 and obtaining pure copper powder by two-stage heat preserving reaction: (1) a first stage: preserving at the temperature of 30-50 DEG C, and converting the Cu(OH)2 into Cu2O after reaction; and (2) a second stage: adjusting pH value of the solution with NaOH to 11-13, heating suspending liquid obtained from the first stage to 60-70 DEG C, keeping the temperature until the reaction is finished to obtain the pure copper powder, and then cleaning and drying the copper powder by centrifugal separation. The raw materials used in the method are cheap and available, and the superfine copper powder with the average particle size below 0.5 micron prepared by the method does not need any anti-oxidation treatment, does not discolor after being kept in the air for more than one year, has anti-oxidation temperature of more than 100 DEG C proved by thermogravimetric analysis and is especially suitable for being used as an electronic material.

Preparation of Ultrafine Copper Powder for MLCC Electrode by Two-Step Reduction

Preparation of ultrafine copper powders by NH2NH2 center dot H2O-HCHO direct reduction method and glucose prereruction method

Progress in Preparation of Ultrafine Copper Powder by Chemical Reduction Method

The Preparation of an Ultrafine Copper Powder by the Hydrogen Reduction of an Ultrafine Copper Oxide Powder and Reduction Kinetics

Preparation and Application of Ultrafine Copper Powder

Study on Preparation of Size-Controllable Spherical Ag Powders with High Tap Density

Preparation method of ultra-low-oxygen spherical micron copper powder

Preparation of Ultrafine Copper Powder with Copper Concentrate

Production of Fine Copper Powder Based on the Theory on Preparation of Monodispersed Particles. Production of fine copper powder by disproportionation reaction of cuprous sulfate solution (2nd Report).

Status-in-art of Preparation and Production of Ultra-fine Copper Powder in China

Method for preparing antioxidated superfine copper powder

Innovative Multiphase Ultrasonic-Assisted Method for High-Purity, Stable, and Cost-Effective Copper Nanowire Synthesis

Preparation and Characterization of Talc/Nano-Cu Conductive Composite Powder

Preparing of Ultrafine Copper Powder by Slurry Electrolysis

Preparation of Monodispersed Copper Nanoparticles by an Environmentally Friendly Chemical Reduction

A simple method for the preparation of Cu 20 with different morphologies in high reaction concentrations

Preparation of copper nano-particle by homogeneous reduction method

A novel method for preparing ultrafine molybdenum powder

Sequential Two-Step Reduction of High-Purity Nano Copper with Glucose and Ascorbic Acid for the Synthesis of Nano Silver-Coated Copper

Preparation of Ultrafine Cu 2 O Powders with Different Morphologies from Cu(OH) 2 Gel

Preparation and Characterization of Silver Powders with Spheric Shape and Different Sizes