Obvious Difference in Fracture Strength and Magnetic Properties by Strip Casting Thickness of NdFeB

Yan Mi,Yu Lianqing,Zhang Wenyong,Wang Wei

DOI: https://doi.org/10.3321/j.issn:1002-185x.2006.07.018

2006-01-01

Rare Metal Materials and Engineering

Abstract:The dependence of fracture strength and magnetic properties of sintered NdFeB magnets on the thickness of strip casting is studied. It is found that the bending strength rapidly increases with the decrease of the thickness of strip casting. A lot of ultra fine grains would be easily oxidized during the jet milling for the thinner strip castings. The oxidization restrains the grain growth effectively, as a result, the grains in the sintered magnets by the thinner strip casting are fine. According to the formula of fracture strength for ceramic materials, the finer the grain, the higher the fracture strength of magnets. For example, the bending strength of the magnets produced by strip casting with a thickness of 0.38 mm is 50% larger than that of 0.45 mm. In addition, the strip casting of 0.45 min in thickness has a more homogeneous distribution of grain size within a range of 3 mu m similar to 5 mu m, near the optimal grain size distribution. So the sintered magnets made of the thinner strip castings possess better magnetic properties.