Magnetic and mechanical properties of grain-refined Dy-free Nd-Fe-B sintered magnets

Wei Tang,Gaoyuan Ouyang,Baozhi Cui,Jing Wang,Kevin W. Dennis,Matthew J. Kramer,Iver E. Anderson,Jun Cui
DOI: https://doi.org/10.1016/j.jmmm.2020.167533
IF: 3.097
2021-03-01
Journal of Magnetism and Magnetic Materials
Abstract:<p>The effects of grain size on magnetic and mechanical properties of Dy-free Nd-Fe-B sintered magnets were studied. The grain size of the sintered magnets was varied by using different sized Dy-free Nd-Fe-B alloy feedstock powders which were ball milled to different extents. Increasing the ball milling time from 7 to 11 hrs caused the average particle size of the powders to decrease from 3.6 to 2.1 µm, while the average grain size of the corresponding sintered magnets decreased from 5.0 to 4.0 µm. The intrinsic coercivity H<sub>cj</sub> and maximum energy product (BH)<sub>max</sub> of these magnets increased from 11.6 to 13.7 kOe and 41.6 to 43.6 MGOe, respectively. The finer grain magnets exhibited better thermal stability, as indicated by a smaller temperature coefficient of H<sub>cj</sub> (-0.71 %/°C). With extending ball milling time to 15 hrs, the magnetic properties of the magnets deteriorate, while the flexural strengths first decrease and thus increase. The flexural strength improvement is attributed to the increased Oxygen content in the magnets due to finer grains. The coercivity enhancement by reduction of grain size is a promising approach to develop Dy-free Nd-Fe-B sintered magnets with better thermal stability. It is important to control the Oxygen contents in the magnets to compromise both magnetic and mechanical properties.</p>
materials science, multidisciplinary,physics, condensed matter
What problem does this paper attempt to address?
The paper primarily investigates the influence of grain size on the magnetic and mechanical properties of dysprosium-free (Dy-free) neodymium-iron-boron (Nd-Fe-B) sintered magnets. The study prepared alloy powders of different sizes by controlling the ball milling time and further produced sintered magnets with varying grain sizes. Specifically: 1. **Research Background and Objectives**: - Nd-Fe-B magnets are widely used in modern green energy technologies due to their high energy density, such as in traction drive motors for hybrid vehicles and wind turbines. - However, these magnets have poor stability at high temperatures and usually require the addition of expensive and scarce heavy rare earth element dysprosium (Dy) to improve their coercivity and thermal stability. - This study aims to explore the development of Dy-free Nd-Fe-B sintered magnets by reducing grain size to achieve better thermal stability and sufficient energy density. 2. **Experimental Methods**: - Hydrogen-decrepitated coarse alloy powder was used as the starting material, and powders with different average particle sizes were obtained through ball milling. - These powders were then oriented in a magnetic field, cold isostatically pressed, and sintered to produce sintered magnet samples with different grain sizes. - The samples were characterized using scanning electron microscopy (SEM), magnetic measurement systems, and other techniques. 3. **Main Findings**: - When the ball milling time increased from 7 hours to 11 hours, the average particle size of the alloy powder decreased from 3.6 micrometers to 2.1 micrometers, and the corresponding average grain size of the sintered magnets decreased from 5.0 micrometers to 4.0 micrometers. - The intrinsic coercivity (\(H_{cj}\)) and maximum energy product \((BH)_{max}\) of the magnets increased from 11.6 kilo-oersteds (kOe) to 13.7 kOe, and from 41.6 MGOe to 43.6 MGOe, respectively. - Magnets with finer grains exhibited better thermal stability, as indicated by a smaller temperature coefficient of \(-0.71\%/\degree C\). - Further extending the ball milling time to 15 hours resulted in a decline in the magnetic properties of the magnets, but the bending strength first decreased and then significantly increased. - The improvement in bending strength was attributed to the increased oxygen content within the magnets, which is related to the finer grains. 4. **Conclusion**: - Reducing grain size is an effective way to enhance the coercivity and thermal stability of Dy-free Nd-Fe-B sintered magnets. - Controlling the oxygen content in the magnets is crucial for balancing magnetic and mechanical properties. In summary, this study demonstrates the potential for improving the performance of Dy-free Nd-Fe-B sintered magnets by adjusting grain size and highlights the importance of further optimizing process parameters (such as ball milling time and conditions).