Abstract:Due to the fluctuation and non-uniform distribution of temperature within the core structure of high-temperature gas-cooled reactors (HTGRs), the thermal expansion behavior of graphite materials plays an important role in the design of graphite components, especially of large-scale components. In the present paper, in order to investigate the influence of stress levels on the coefficient of thermal expansion (CTE) of IG-110 graphite, the strain gauge method was used to measure the CTE on the cylindrical specimens under a series of loads applied using a universal tensile testing machine. In addition, a more precise measurement using a thermal dilatometer was employed to validate the tests using the strain gauge method. A good agreement has been obtained between the experimental results using these two methods. The results show that when the specimens were under compressive loads, the CTE along the loading direction of the specimens increased and that along the perpendicular direction decreased, with more changes in the former. The absolute changes of the CTE in the two directions increased with increasing applied load. When graphite specimens were subjected to a compressive load of 40MPa, the axial CTE of specimens sectioned along the radial direction of the graphite brick as it is installed in the core structure increased from 4.13×10−6 to 5.35×10−6K−1, while the axial CTE of specimens sectioned along the vertical direction increased from 3.97×10−6 to 5.58×10−6K−1. Moreover, the residual change of the CTE, which was caused by the permanent residual strain after unloading, was observed. The change of the CTE with stress levels should be considered in the stress analysis and life prediction of the nuclear graphite components.

Measurement and Validation of Coefficient of Thermal Expansion of Graphite IG-110 under Compressive Stress

Anisotropy of Coefficient of Thermal Expansion of Nuclear Graphite under Compressive Stresses

The Effect of Stress Levels on the Coefficient of Thermal Expansion of a Fine-Grained Isotropic Nuclear Graphite

Modelling the coefficient of thermal expansion in graphite crystals: implications of lattice strain due to irradiation and pressure

Inverse Identification of Tensile and Compressive Damage Properties of Graphite Material Based on a Single Four-Point Bending Test

Effects of Tensile and Compressive Stresses on Damage Evolution Law of Nuclear Graphite

The coefficient of thermal expansion of nuclear graphite with increasing thermal oxidation

The effect of thermal oxidation on the coefficient of thermal expansion of nuclear graphite

Experimental Study on Dynamic Tensile Strength of Graphite

Measurement of Tensile Strength of Nuclear Graphite Based on Ring Compression Test

Investigating the Effects of Confining Pressure on Graphite Material Failure Modes and Strength Criteria

Dynamic Fracture Toughness Measurement of Graphite Material Considering Inertial Effect

Coefficient of thermal expansion of nanostructured tungsten based coatings assessed by thermally induced substrate curvature method

Coefficient of thermal expansion of nanostructured tungsten based coatings assessed by substrate curvature method

Experimental and Simulation Study on Stress Concentration of Graphite Components in Tension

An Experimental Study On Fracture Toughness Of A Fine-Grained Isotropic Graphite

Experimental Investigations On Tensile Strength Of Chinese Nuclear Graphite

Combined evaluation of Young modulus and fracture toughness in small specimens of fine grained nuclear graphite using 3D image analysis

An investigation of fracture behaviors of NBG-18 nuclear graphite using in situ mechanical testing coupled with micro-CT

Parameters Measurement of Nuclear Graphite Based on Digital Image Correlation

A review of the coefficient of thermal expansion and thermal conductivity of graphite