Abstract:Graphite materials play critical roles as moderators, reflectors, and core structural components in high-temperature gas-cooled nuclear reactors. During the reactor operation, graphite materials may experience a variety of loads, including thermal, radiation, fatigue, and dynamic loads, potentially leading to crack initiation and propagation. Therefore, it is imperative to investigate their fracture properties. Despite this, there remains a paucity of comprehensive studies on the fracture toughness of graphite materials with varying grain sizes, particularly concerning dynamic fracture toughness. This study addresses this gap by employing a digital-image-correlation-based virtual extensometer to analyze crack propagation in graphite materials of different grain sizes, enabling precise measurement of crack propagation length and fracture toughness. Findings reveal that static fracture toughness increases with larger grain sizes, while under dynamic loading, smaller grain sizes exhibit greater fracture toughness. Additionally, dynamic fracture toughness shows a near-linear increase with impact speed. Scanning electron microscopy analysis of fracture surface morphology highlights the impact of grain size and impact speed on fracture toughness. Nuclear graphite specimens with larger grain sizes have more irregular grain and pore distributions, enhancing crack deflection and propagation resistance, thereby increasing fracture toughness. The observed loading rate dependence of dynamic fracture toughness is attributed to a gradual transition from intergranular to transgranular fracture modes with increasing impact speed.

Measurement of Tensile Strength of Nuclear Graphite Based on Ring Compression Test

Determination of Tensile Strength by Modified Brazilian Disc Method for Nuclear Graphite

Effects of damage evolution on tensile strength measurement of nuclear graphite material by ring compression test

Experimental Investigations On Tensile Strength Of Chinese Nuclear Graphite

Effects of Tensile and Compressive Stresses on Damage Evolution Law of Nuclear Graphite

Inverse Identification of Tensile and Compressive Damage Properties of Graphite Material Based on a Single Four-Point Bending Test

Experimental Study on Dynamic Tensile Strength of Graphite

Parameters Measurement of Nuclear Graphite Based on Digital Image Correlation

Dynamic Fracture Toughness Measurement of Graphite Material Considering Inertial Effect

Experimental and Simulation Study on Stress Concentration of Graphite Components in Tension

A New Method to Measure Crack Extension in Nuclear Graphite Based on Digital Image Correlation

Evaluating the dynamic fracture toughness of graphite via accurate determination of the dynamic crack propagation length

Measurement and Validation of Coefficient of Thermal Expansion of Graphite IG-110 under Compressive Stress

Investigating the Effects of Confining Pressure on Graphite Material Failure Modes and Strength Criteria

Combined evaluation of Young modulus and fracture toughness in small specimens of fine grained nuclear graphite using 3D image analysis

Domestic Graphite Strength Test for HTR Engineering Verification

An investigation of fracture behaviors of NBG-18 nuclear graphite using in situ mechanical testing coupled with micro-CT

Static and Dynamic Fracture Toughness of Graphite Materials with Varying Grain Sizes

Study on Failure Mechanism of Line Contact Structures of Nuclear Graphite

Anisotropy of Coefficient of Thermal Expansion of Nuclear Graphite under Compressive Stresses

Analysis of Crack Propagation in Nuclear Graphite Using Three-Point Bending of Sandwiched Specimens