Secondary Hardening and Dislocation Evolution in Low Cycle Fatigue of Polycrystalline Aluminium

YB XIA,ZG WANG,RH WANG

DOI: https://doi.org/10.1002/pssa.2211200110

1990-01-01

physica status solidi (a)

Abstract:Cyclic deformation of well annealed 99.999% pure Al and 99.85% commercially pure Al polycrystals is performed under constant total strain and plastic strain control, respectively. The stress response to cyclic loading is measured and secondary hardening occurs in a certain range of strain amplitudes. The evolution of dislocation microstructures and surface slip appearances during cyclic deformation are examined by TEM and SEM, respectively. It is noted that the secondary hardening is dependent on microstructural changes taking place in cyclic loading, such as the activation of secondary slip systems and the formation of a dislocation cell structure with increasing misorientations and decreasing cell sizes. Grain boundaries promote an early occurrence of secondary hardening and enhance its strength. Zyklische Belastungsmessungen an gut ausgeheilten 99,999% reinen Al- und 99,85% reinen, kommerziellen Al-Polykristallen werden unter konstanter Gesamtdehnung bzw. Steuerung der plastischen Dehnung durchgeführt. Das Spannungsverhalten gegenüber zyklischer Belastung wird gemessen und es tritt sekundäre Verfestigung in einem gewissen Bereich der Dehnungsamplitude auf. Die Entwicklung von Versetzungsmikrostrukturen und Oberflächengleitung während der zyklischen Deformation werden mittels TEM bzw. SEM untersucht. Es wird festgestellt, daß die sekundäre Verfestigung von mikrostrukturellen Änderungen abhängt, die bei zyklischer Belastung auftreten, wie die Aktivierung von sekundären Slipsystemen und die Bildung einer Versetzungszellenstruktur mit wachsender Fehlorientierung und abnehmender Zellengröße. Korngrenzen fördern ein frühes Auftreten von sekundärer Verfestigung und erhöhen dessen Stärke.