Abstract:It is known that Si3N4 shows excellent tribological properties in water. This is attributed to the hydrolysis of Si3N4 itself. The glassy phase content in Si3N4 is considered to be an important factor affecting the hydrolysis of Si3N4 during friction. In the present paper the effect of glassy phase content in silicon nitride against grey iron in water on its tribological characteristics was investigated. Distilled water and a dilute aqueous solution of sodium silicate were used as lubricants. The experiments were carried out on a type MM-200 wear tester. The total wear displacements of two samples were also monitored on-line to obtain total wear data. When distilled water is used as lubricant, the Si3N4/grey iron sliding pairs with 5 wt.% oxide additives into Si3N4, their friction coefficients decrease to 0.02 and the wear losses of the pairs also are the smallest of all test pairs after 10 km of sliding. With increasing 10 wt.% additives into Si3N4 the friction coefficient of the sliding pairs falls down during the test, but their values do not reach 0.02. The wear of the sliding pairs after 10 km of sliding is also quite small, compared to other test pairs with 15, 20 and 30 wt.%. When dilute aqueous sodium silicate solution is used as lubricant, the friction coefficient values for all test pairs decrease to 0.02 before 4 km of sliding. Their wears after 10 km are also much lower than with lubrication by distilled water. The wear differences among all test pairs are not significant, which indicates that the possibility of tribochemical reaction is identical for all samples with different oxide additive content in this case. On the other hand, sodium silicate, as an excellent corrosion-inhibitive agent for iron can efficiently delay the iron rust during lubrication and extends the commercial application of water as a lubricant.

Tribology of Si3N4 with Different Glassy Phase Content Sliding Against Grey Cast Iron Lubricated with Water

Tribological Characteristics of Silicon Nitride-chilled Cast Iron with Oil-less Lubrication

Friction and Wear of Self-Mated SiC and Si 3 N 4 in Green Water-Based Lubricant

Effect of Inhibitors on Tribological Characteristics of Gray Cast Iron Sliding against Si3N4 Ceramic

Investigation on the components and the formation of a tribochemical film in the Si3N4–gray iron sliding pair lubricated with distilled water

Friction and Wear Properties of Si3N4 and SiC Used for Water-Lubricated Sliding Bearings

Analysis on Wear Properties and Impact Factors for Si3N4 Ceramic Mated with Chilled Cast Iron

Air and water lubricated sliding wear of Si3N4 against cast irons

The Effect of Inhibitors on the Corrosion and Tribological Characteristics of Gray Iron Sliding Against Si3n4 under Lubricated Conditions

An investigation on component and formation of tribochemical film in Si3N4-white iron sliding pair lubricated with distilled water

Friction and wear of grey cast iron against Si3N4 in emulsion and water

Tribological Properties of Si3n4 Sliding Against Bearing Steel under Different Conditions

Investigation on formation of tribo-film in Si3N4-gray iron sliding pair lubricated with Na2SiO3 inhibited solution

Tribochemical Behavior of Si 3 N 4 –hbn Ceramic Materials with Water Lubrication

Tribological Behavior and Lubricating Mechanism of Si3N4 in Artificial Seawater

Tribological Characterization of Several Silicon-Based Materials under Ionic-Liquids Lubrication

Research on Tribology Property of Si-3N-4 Ceramic and Chilled Iron under Oil-Less Lubrication

Study on the friction and wear properties of Si3N4-high speed steel lubricated by several lubricants

Tribological Properties of Cr(Si)CN Coatings Sliding Against Different Mating Balls in Water

The effect of tribofilm formation on the tribological characteristics of ceramic-cast iron sliding pairs

Effect of lubricants on the friction and wear of Al2O3 against gray cast iron