Corrosion Behavior of 1420Al-Li Alloy under Tensile Stress

CHEN Wen-jing,LI Jin-feng,ZHAO Xu-shan,REN Wen-da,ZHENG Zi-qiao
DOI: https://doi.org/10.3969/j.issn.1673-9981.2007.02.008
2007-01-01
Abstract:The corrosion behavior of 2195 and 1420 Al-Li alloy under applied tensile stress in neutral 3.5% NaCl solution were investigated by potentiodynamic polarization curves,SEM and TEM.It shows that uniform corrosion with large and discrete pits occured on unstressed 1420 alloy,while the corrosion on unstressed 2195 alloy were general corrosion and localized corrosion including intergranular corrosion and pitting corrosion.As stress was applied to 1420 alloy,the pit became denser and smaller.For stressed 2195 alloy,intergranular corrosion was greatly aggravated and severe general corrosion was developed from connected pits.